The productivity of the chrome-containing semi-steel converter smelting process is directly affected by the slag-forming speed during the converter preliminary stage.The effects of Cr_(2)O_(3) content on the physicoch...The productivity of the chrome-containing semi-steel converter smelting process is directly affected by the slag-forming speed during the converter preliminary stage.The effects of Cr_(2)O_(3) content on the physicochemical properties of the CaO-SiO_(2)-Fe_(t)O-MgO system,such as melting temperature,solidification behavior,mineral composition,and lime dissolution rate,were studied.The results showed that the slag was an amorphous phase at 1500℃.When Cr_(2)O_(3) was added,Ca(Fe,Mg)Si_(2)O_(6) and spinel were formed in the slag.With the increase in Cr_(2)O_(3) content,the amount of spinel precipitation increased,and the dendritic FegO_(4) crystal gradually changed into the granular(Fe,Mg)(Fe,Cr)2O_(4) crystal.As the Cr_(2)O_(3) content increased from O to 2.91 wt.%,the melting temperature of the slag rose,and the melting range of the slag expanded slightly,but the lime dissolution rate did not change.When the Cr_(2)O_(3) content further increased to 9.09 wt.%,the melting temperature continued to rise,the melting range rapidly expanded,and the lime dissolution rate decreased.展开更多
基金supported by the National Natural Science Foundation of China(Nos.52074197 and 51974210)Hubei Provincial Natural Science Foundation(No.2019CFB697)State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology.
文摘The productivity of the chrome-containing semi-steel converter smelting process is directly affected by the slag-forming speed during the converter preliminary stage.The effects of Cr_(2)O_(3) content on the physicochemical properties of the CaO-SiO_(2)-Fe_(t)O-MgO system,such as melting temperature,solidification behavior,mineral composition,and lime dissolution rate,were studied.The results showed that the slag was an amorphous phase at 1500℃.When Cr_(2)O_(3) was added,Ca(Fe,Mg)Si_(2)O_(6) and spinel were formed in the slag.With the increase in Cr_(2)O_(3) content,the amount of spinel precipitation increased,and the dendritic FegO_(4) crystal gradually changed into the granular(Fe,Mg)(Fe,Cr)2O_(4) crystal.As the Cr_(2)O_(3) content increased from O to 2.91 wt.%,the melting temperature of the slag rose,and the melting range of the slag expanded slightly,but the lime dissolution rate did not change.When the Cr_(2)O_(3) content further increased to 9.09 wt.%,the melting temperature continued to rise,the melting range rapidly expanded,and the lime dissolution rate decreased.