A series of single phase,warm white light emitting phosphors,Gd(P_(x)V_(1−x))O_(4):y at%Sm^(3+),with 1 at%Bi^(3+) doping concentration were synthesized by high temperature solid state method in this work.The experimen...A series of single phase,warm white light emitting phosphors,Gd(P_(x)V_(1−x))O_(4):y at%Sm^(3+),with 1 at%Bi^(3+) doping concentration were synthesized by high temperature solid state method in this work.The experimental results indicate broadband cyan emission of Bi^(3+)and characteristic orange-red emission of Sm^(3+)can be effectively tuned by changing the ratios of PO^(3−)_(4)/VO^(3−)_(4) in Gd(P_(x)V_(1−x))O_(4):1 at%Sm^(3+),1 at%Bi^(3+),and the energy transfer process among VO^(3−)_(4),Sm^(3+),Bi^(3+) also can be adjusted.Based on this,warm white light emitting can be realized by further optimizing the doping concentration of Sm^(3+) in the phosphors.At 423 K,the PL intensity of Gd(P_(0.7)V_(0.3))O_(4):2 at%Sm^(3+),1 at%Bi^(3+) remains~84.3%of the initial value at 293 K,while the measured quantum efficiency is 67.8%.EL spectrum analysis results of the fabricated white light emitting diode(wLED)based on a 310 nm UV-chip and Gd(P_(0.7)V_(0.3))O4:2 at%Sm^(3+),1 at%Bi^(3+)phosphors imply low correlated color temperature(3132 K)and appropriate color-rending index(R_(a)=82.7).These results demonstrate that Gd(P_(0.7)V_(0.3))O4:2 at%Sm^(3+),1 at%Bi^(3+)is a good candidate for manufacturing UV-activated warm white light emitting diodes.展开更多
FTIR absorption spectra indicate that H^+can easily enter the crystal structure and form OH^-centers in Er:Yb:YCOB and O-H bonds prefer to lie in the a-c plane.Within our current studied concentration level,crystal sa...FTIR absorption spectra indicate that H^+can easily enter the crystal structure and form OH^-centers in Er:Yb:YCOB and O-H bonds prefer to lie in the a-c plane.Within our current studied concentration level,crystal samples with higher OH-abso rption coefficie nts demonstrate stro nger fluo rescence intensity and longer fluorescence lifetime at 1535 nm.As the stretching vibration energy of OH-group approximately corresponds to the energy gap between the 4 I11/2 and 4 I13/2 levels of Er^3+,and thus,OH^-ions can shorten the fluorescence lifetime of Er^3+-4I11/2 level by the phonon-assisted cross-relaxation process between the Er^3+and OH-ions.Our curre nt results confirm that a certain conte nt of OH ions can enhance the ene rgy transfer process from Yb^3+to Er^3+and subsequently promote fluorescence output in 1.5-1.6μm.展开更多
基金Project supported by the National Natural Science Foundation of China(51972181,61705231)Major Basic Research Projects of Shandong Natural Science Foundation(ZR2018ZB0650)+2 种基金China Postdoctoral Science Foundation(2015M580573)High Quality Course Construction Project of Graduate Education in Shandong Province(SDYKC18051)Postgraduate Tutor Ability Improvement Project of Shandong Province(SDYY17179)。
文摘A series of single phase,warm white light emitting phosphors,Gd(P_(x)V_(1−x))O_(4):y at%Sm^(3+),with 1 at%Bi^(3+) doping concentration were synthesized by high temperature solid state method in this work.The experimental results indicate broadband cyan emission of Bi^(3+)and characteristic orange-red emission of Sm^(3+)can be effectively tuned by changing the ratios of PO^(3−)_(4)/VO^(3−)_(4) in Gd(P_(x)V_(1−x))O_(4):1 at%Sm^(3+),1 at%Bi^(3+),and the energy transfer process among VO^(3−)_(4),Sm^(3+),Bi^(3+) also can be adjusted.Based on this,warm white light emitting can be realized by further optimizing the doping concentration of Sm^(3+) in the phosphors.At 423 K,the PL intensity of Gd(P_(0.7)V_(0.3))O_(4):2 at%Sm^(3+),1 at%Bi^(3+) remains~84.3%of the initial value at 293 K,while the measured quantum efficiency is 67.8%.EL spectrum analysis results of the fabricated white light emitting diode(wLED)based on a 310 nm UV-chip and Gd(P_(0.7)V_(0.3))O4:2 at%Sm^(3+),1 at%Bi^(3+)phosphors imply low correlated color temperature(3132 K)and appropriate color-rending index(R_(a)=82.7).These results demonstrate that Gd(P_(0.7)V_(0.3))O4:2 at%Sm^(3+),1 at%Bi^(3+)is a good candidate for manufacturing UV-activated warm white light emitting diodes.
基金Project supported by the National Natural Science Foundation of China(11204148,11374170)Major Basic Research Projects of Shandong Natural Science Foundation(ZR2018ZB0650)+4 种基金China Postdoctoral Science Foundation(2015M580573)the Applied Basic Research Programs for Youths of Qingdao(15-9-1-52-JCH)Taishan Scholar Program of Shandong Provincethe Qingdao Postdoctoral Application Research Project(2015127)the Open Projects of State Key Laboratory of Rare-earth Resource Utilization(RERU2016015)
文摘FTIR absorption spectra indicate that H^+can easily enter the crystal structure and form OH^-centers in Er:Yb:YCOB and O-H bonds prefer to lie in the a-c plane.Within our current studied concentration level,crystal samples with higher OH-abso rption coefficie nts demonstrate stro nger fluo rescence intensity and longer fluorescence lifetime at 1535 nm.As the stretching vibration energy of OH-group approximately corresponds to the energy gap between the 4 I11/2 and 4 I13/2 levels of Er^3+,and thus,OH^-ions can shorten the fluorescence lifetime of Er^3+-4I11/2 level by the phonon-assisted cross-relaxation process between the Er^3+and OH-ions.Our curre nt results confirm that a certain conte nt of OH ions can enhance the ene rgy transfer process from Yb^3+to Er^3+and subsequently promote fluorescence output in 1.5-1.6μm.