This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid...This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid) resin. In this research, effect of molding temperature and fiber content on flexural properties of bamboo fiber reinforced composites was investigated. The flexural strength of this composite increased with increasing fiber content up to 70%. The flexural strength of composites decreased at molding temperature of 180°C. Biodegradable composites possessed extremely high flexural strength of 273 MPa, in the case of molding temperature of 160°C and fiber content of 70%.展开更多
Natural plant fibers, including flax, kenaf, jute, bamboo, ramie and much more are renewable and sustainable resources and are considered good candidates for cost-effective alternatives to glass and carbon fibers. In ...Natural plant fibers, including flax, kenaf, jute, bamboo, ramie and much more are renewable and sustainable resources and are considered good candidates for cost-effective alternatives to glass and carbon fibers. In this research, cross ply biodegradable composites were fabricated by press-forming method. The biodegradable composites consist of Manila hemp textile as a reinforcement and starch-based biodegradable plastics as a matrix was fabricated and investigated about mechanical properties. The tensile strength increased with the fiber content until fiber content of about 50% and leveled off thereafter. This dependence on the fiber content is due to the decrease in fiber strength of loading direction caused by fiber damages introduced during hot-pressing. In order to decrease the damage of fibers aligned in loading direction, Manila hemp textile was produced by using Manila hemp fibers for warp and biodegradable resin thread for weft. As a result, the tensile strength of cross ply composites increased from 153 MPa to 202 MPa.展开更多
This paper describes the mechanical properties of the composite materials produced using long bamboo fiber and bamboo powder. Bamboo fiber and powder can be hot press-molded much like plastic materials, and the use of...This paper describes the mechanical properties of the composite materials produced using long bamboo fiber and bamboo powder. Bamboo fiber and powder can be hot press-molded much like plastic materials, and the use of these materials in place of plastic products would reduce the environmental impact of extensive plastic use. In this study, the tensile and flexural properties of molded uni-directional long fiber reinforced composites made from bamboo fiber bundles and Bamboo powder were examined. The results showed that the tensile and flexural strength of bamboo fiber/powder composites were increased with increasing fiber content. On the other side, both strengths of composite were decreased with increasing molding temperature after 180℃. The highest tensile and flexural strengths of the bamboo fiber reinforced bamboo powder composites specimens which were tested were recorded at 169.9 MPa and 221.1 MPa, respectively.展开更多
文摘This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid) resin. In this research, effect of molding temperature and fiber content on flexural properties of bamboo fiber reinforced composites was investigated. The flexural strength of this composite increased with increasing fiber content up to 70%. The flexural strength of composites decreased at molding temperature of 180°C. Biodegradable composites possessed extremely high flexural strength of 273 MPa, in the case of molding temperature of 160°C and fiber content of 70%.
文摘Natural plant fibers, including flax, kenaf, jute, bamboo, ramie and much more are renewable and sustainable resources and are considered good candidates for cost-effective alternatives to glass and carbon fibers. In this research, cross ply biodegradable composites were fabricated by press-forming method. The biodegradable composites consist of Manila hemp textile as a reinforcement and starch-based biodegradable plastics as a matrix was fabricated and investigated about mechanical properties. The tensile strength increased with the fiber content until fiber content of about 50% and leveled off thereafter. This dependence on the fiber content is due to the decrease in fiber strength of loading direction caused by fiber damages introduced during hot-pressing. In order to decrease the damage of fibers aligned in loading direction, Manila hemp textile was produced by using Manila hemp fibers for warp and biodegradable resin thread for weft. As a result, the tensile strength of cross ply composites increased from 153 MPa to 202 MPa.
文摘This paper describes the mechanical properties of the composite materials produced using long bamboo fiber and bamboo powder. Bamboo fiber and powder can be hot press-molded much like plastic materials, and the use of these materials in place of plastic products would reduce the environmental impact of extensive plastic use. In this study, the tensile and flexural properties of molded uni-directional long fiber reinforced composites made from bamboo fiber bundles and Bamboo powder were examined. The results showed that the tensile and flexural strength of bamboo fiber/powder composites were increased with increasing fiber content. On the other side, both strengths of composite were decreased with increasing molding temperature after 180℃. The highest tensile and flexural strengths of the bamboo fiber reinforced bamboo powder composites specimens which were tested were recorded at 169.9 MPa and 221.1 MPa, respectively.