ZIF-8-based micro-arc oxidation composite coatings enhanced the corrosion resistance and superhydrophobicity of a Mg alloy

Mg alloys are considered the most promising engineering materials because of their unique properties.However,the uncontrolled corrosion rate of these alloys limits their applications.Therefore,in this study,a micro-arc oxidation layer was used as a transition layer to“directly”grow a zinc-based metal-organic framework(MOF)composite coating on the surface of a Mg alloy(AZ91D).Herein,the two zeolitic imidazolate framework(ZIF-8)coatings with different morphologies were separately prepared by homologous metal oxide induction and a one-step in-situ growth method.The superhydrophobic composite coating showed strong hydrophobicity and self-cleaning properties,which could prevent the penetration of water and corrosive ions(Cl^(−))into the surface of AZ91D.Electrochemical tests demonstrated that the super-hydrophobic composite coatings greatly enhanced the corrosion resistance of AZ91D,and the corrosion current density decreased from 10^(−5)to 10^(−9)A/cm^(2).These results indicate that the ZIF-8 coatings are beneficial for improving the hydrophobicity and enhancing the corrosion resistance of Mg alloys.Therefore,MOF composite coatings provide a new strategy that can be used to prepare multifunctional anticorrosion coatings on metal substrates.

ZnO@ZIF-8 core-shell structure nanorods superhydrophobic coating on magnesium alloy with corrosion resistance and self-cleaning

A longstanding quest in material science has been the development of superhydrophobic coating based on a single material, without the requirement of fluorination or silane treatment. In this work, the micro-arc oxidation(MAO) coating as transition layer can effectively enhance the bonding force of the superhydrophobic coating. The semiconductor@metal organic frameworks(MOFs) core-shell structure was synthesized by a simple self-templating method, and obtained ZnO@2-methylimidazole zinc salt(ZIF-8) nanorods array on magnesium(Mg)alloy. ZnO nanorods not only act as the template but also provide Zn^(2+) for ZIF-8. In addition, we proved that the ligand concentration,synthesis time and temperature are the keys to the preparation of ZnO@ZIF-8 nanorods. As we expect, the ZnO@ZIF-8 nanorods array can trap air in the gaps to form an air layer, and the coating exhibits superhydrophobic properties(154.81°). Excitingly, ZnO@ZIF-8 nanorods array shown a superhydrophobic property, without the requirement of fluorination or silane treatment. The results shown that the coating has good chemical stability and self-cleaning performance. Meanwhile, the corrosion resistance has been significantly improved, R_(ct) was increased from 1.044×10^(3) to 1.414×10^(6) Ω/cm^(2) and I_(corr) was reduced from 4.275×10^(-5) to 5.611×10^(-9)A/cm^2. Therefore, the semiconductor@MOFs core-shell structure has broad application prospects in anti-corrosion.