Photoresponsive linear liquid crystal polymers(LLCPs)are attractive because of the excellent stimuli-responsibility and the good processability.In this study,a new photoresponsive LLCP containing azoester(PC11AE6)with...Photoresponsive linear liquid crystal polymers(LLCPs)are attractive because of the excellent stimuli-responsibility and the good processability.In this study,a new photoresponsive LLCP containing azoester(PC11AE6)with good mesophase stability was synthesized by ringopening metathesis polymerization.By introducing photoresponsive azoester mesogenic unit,which has high rigidity and a large lengthdiameter ratio,the resultant polymer possesses a broad mesophase temperature interval(isotropic temperature=180℃).A study on mesophase by 2D-wide angle X-ray diffraction indicated that the mesogens were orientated spontaneously into smectic A phase after annealing.The orientated films and fibres exhibited macroscopic,rapid and reversible deformations under light irradiation as a result of the photoisomerization of azoester as confirmed by UV-Vis absorption spectrophotometry.We anticipate that this work provides a strategy for preparing LLCP with a broad mesophase temperature range,which is positive for potential applications.展开更多
基金This work was financially supported by the National Natural Science Foundation of China(Nos.21734003,51573029,51721002)Natural Science Foundation of Shanghai(No.17ZR1440100)Innovation Program of Shanghai Municipal Education Commission(No.2017-01-07-00-07-E00027).
文摘Photoresponsive linear liquid crystal polymers(LLCPs)are attractive because of the excellent stimuli-responsibility and the good processability.In this study,a new photoresponsive LLCP containing azoester(PC11AE6)with good mesophase stability was synthesized by ringopening metathesis polymerization.By introducing photoresponsive azoester mesogenic unit,which has high rigidity and a large lengthdiameter ratio,the resultant polymer possesses a broad mesophase temperature interval(isotropic temperature=180℃).A study on mesophase by 2D-wide angle X-ray diffraction indicated that the mesogens were orientated spontaneously into smectic A phase after annealing.The orientated films and fibres exhibited macroscopic,rapid and reversible deformations under light irradiation as a result of the photoisomerization of azoester as confirmed by UV-Vis absorption spectrophotometry.We anticipate that this work provides a strategy for preparing LLCP with a broad mesophase temperature range,which is positive for potential applications.