Al/Ni multilayer composites are produced by accumulative roll bonding process and then annealed with different temperatures and time.Macroscopic images,microstructure and mechanical properties of Al/Ni multilayer comp...Al/Ni multilayer composites are produced by accumulative roll bonding process and then annealed with different temperatures and time.Macroscopic images,microstructure and mechanical properties of Al/Ni multilayer composites are investigated.As for the macroscopic images,although there was an edge crack along the rolling direction at the third pass,the defect of composites was not serious and the forming quality of composites was relatively good.The yield strength and elongation of Al/Ni multilayer composites are improved after the annealing treatment;however,with the increase in annealing temperature and time,the yield strength and ciongation of Al/Ni multilayer composites are decreased.During the process of annealing treatment,aluminum atoms diffuse in the way of vacancy diffusion,which results in the formation of Al3Ni intermetallic phase at Al/Ni interface and Kirkendall void in the aluminum side.The content of Al3Ni intermetallic phase and Kirkenckill void would increase with the increase in annealing temperature and time.展开更多
基金This research is sponsored by the National Natural Science Foundation of China(NSFC 51605307)the Scientific Research Foundation of the Education Department of Liaoning Province,China(LGD2016020).
文摘Al/Ni multilayer composites are produced by accumulative roll bonding process and then annealed with different temperatures and time.Macroscopic images,microstructure and mechanical properties of Al/Ni multilayer composites are investigated.As for the macroscopic images,although there was an edge crack along the rolling direction at the third pass,the defect of composites was not serious and the forming quality of composites was relatively good.The yield strength and elongation of Al/Ni multilayer composites are improved after the annealing treatment;however,with the increase in annealing temperature and time,the yield strength and ciongation of Al/Ni multilayer composites are decreased.During the process of annealing treatment,aluminum atoms diffuse in the way of vacancy diffusion,which results in the formation of Al3Ni intermetallic phase at Al/Ni interface and Kirkendall void in the aluminum side.The content of Al3Ni intermetallic phase and Kirkenckill void would increase with the increase in annealing temperature and time.