All-inorganic CsPbI_(2)Br perovskite solar cells(PSCs)have received extensive research interests recently.Nevertheless,their low efficiency and poor long-term stability are still obstacles for further commercial appli...All-inorganic CsPbI_(2)Br perovskite solar cells(PSCs)have received extensive research interests recently.Nevertheless,their low efficiency and poor long-term stability are still obstacles for further commercial application.Herein,we demonstrate that high efficiency and exceptional long-term stability are realized by incorporating gadolinium(III)chloride(GdCl_(3))into the CsPbI_(2)Br perovskite film.The incorporation of GdCl_(3) enhances the Goldschmidt tolerance factor of CsPbI_(2)Br perovskite,yielding a dense perovskite film with small grains,thus the a-phase CsPbI_(2)Br is remarkably stabilized.Additionally,it is found that the GdCl_(3)-incorporated perovskite film achieves suppressed charge recombination and appropriate energy level alignment compared with the pristine CsPbI_(2)Br film.The noticeable increment in efficiency from14.01%(control PSC)to 16.24%is achieved for GdCl_(3)-incorporated PSC.Moreover,the nonencapsulated GdCl_(3)-incorporated PSC exhibits excellent environmental and thermal stability,remaining over 91%or90%of the original efficiency after 1200 h aging at 40%relative humidity or 480 h heating at 85℃ in nitrogen glove box respectively.The encapsulated GdCl_(3)-incorporated PSC presents an improved operational stability with over 88%of initial efficiency under maximum power point(MPP)tracking at 45℃ for1000 h.This work presents an effective ion-incorporation approach for boosting efficiency and long-term stability of all-inorganic PSCs.展开更多
基金supported by the National Natural Science Foundation of China(52172237,52072228)the Shaanxi International Cooperational Project(2020KWZ-018)+1 种基金the Research Fund of the State Key Laboratory of Solidification Processing(NPU),China(Grant No.2021-QZ-02)the Fundamental Research Funds for the Central Universities(3102019JC005)。
文摘All-inorganic CsPbI_(2)Br perovskite solar cells(PSCs)have received extensive research interests recently.Nevertheless,their low efficiency and poor long-term stability are still obstacles for further commercial application.Herein,we demonstrate that high efficiency and exceptional long-term stability are realized by incorporating gadolinium(III)chloride(GdCl_(3))into the CsPbI_(2)Br perovskite film.The incorporation of GdCl_(3) enhances the Goldschmidt tolerance factor of CsPbI_(2)Br perovskite,yielding a dense perovskite film with small grains,thus the a-phase CsPbI_(2)Br is remarkably stabilized.Additionally,it is found that the GdCl_(3)-incorporated perovskite film achieves suppressed charge recombination and appropriate energy level alignment compared with the pristine CsPbI_(2)Br film.The noticeable increment in efficiency from14.01%(control PSC)to 16.24%is achieved for GdCl_(3)-incorporated PSC.Moreover,the nonencapsulated GdCl_(3)-incorporated PSC exhibits excellent environmental and thermal stability,remaining over 91%or90%of the original efficiency after 1200 h aging at 40%relative humidity or 480 h heating at 85℃ in nitrogen glove box respectively.The encapsulated GdCl_(3)-incorporated PSC presents an improved operational stability with over 88%of initial efficiency under maximum power point(MPP)tracking at 45℃ for1000 h.This work presents an effective ion-incorporation approach for boosting efficiency and long-term stability of all-inorganic PSCs.