A new dual-composition catalyst based on Ni-Mo/MgO with high efficiency of producing carbon nanotubes （CNTs） from methane was reported recently. In the present article, with this type of catalyst, the impact of such...A new dual-composition catalyst based on Ni-Mo/MgO with high efficiency of producing carbon nanotubes （CNTs） from methane was reported recently. In the present article, with this type of catalyst, the impact of such experimental parameters as reaction temperature, reaction time, concentration of H2, flow rate ratio of CH4 to H2 on yield and graphitization were investigated, leading to the following optimal growth conditions： reaction time 60min, reaction temperature 900℃, CH4：H2 about 100：20mL/min, under which high-yield multi-walled CNTs bundles were synthesized. Raman measurement indicated that the as-synthesized product was well-graphitized, and the purity was estimated over 95% by TG-DSC analysis. In terms of the above results, an explanation of high-efficiency formation of CNTs bundles and the co-catalysis mechanism of Ni-Mo/MgO were suggested. 2007 Chinese Societv of Particuology and Institute of Process Engineering, Chinese Academy of Sciences. Published by Elsevier B.V.展开更多
基金This work was supported financially by the National Natural Science Foundation of China （No. 20506010） Beijing Novel Program （2006A74）Natural Science Fund of Shanxi Province （No. 20063004）.
文摘A new dual-composition catalyst based on Ni-Mo/MgO with high efficiency of producing carbon nanotubes （CNTs） from methane was reported recently. In the present article, with this type of catalyst, the impact of such experimental parameters as reaction temperature, reaction time, concentration of H2, flow rate ratio of CH4 to H2 on yield and graphitization were investigated, leading to the following optimal growth conditions： reaction time 60min, reaction temperature 900℃, CH4：H2 about 100：20mL/min, under which high-yield multi-walled CNTs bundles were synthesized. Raman measurement indicated that the as-synthesized product was well-graphitized, and the purity was estimated over 95% by TG-DSC analysis. In terms of the above results, an explanation of high-efficiency formation of CNTs bundles and the co-catalysis mechanism of Ni-Mo/MgO were suggested. 2007 Chinese Societv of Particuology and Institute of Process Engineering, Chinese Academy of Sciences. Published by Elsevier B.V.