Tin-based materials are very attractive anodes because of their high theoretical capacity,but their rapid capacity fading from volume expansions limits their practical applications during alloying and dealloying proce...Tin-based materials are very attractive anodes because of their high theoretical capacity,but their rapid capacity fading from volume expansions limits their practical applications during alloying and dealloying processes.Herein,the improved binder-free tin-copper intermetallic/carbon nanotubes(Cu6Sn5/CNTs)alloy thin-film electrodes are directly fabricated through efficient in situ electrodeposition from the leaching solution of treated waste-printed circuit boards(WPCBs).The characterization results show that the easily agglomerated Cu6Sn5 alloy nanoparticles are uniformly dispersed across the three-dimensional network when the CNTs concentration in the electrodeposition solution is maintained at 0.2 g·L−1.Moreover,the optimal Cu6Sn5/CNTs-0.2 alloy thin-film electrode can not only provide a decent discharge specific capacity of 458.35 mAh·g^(−1)after 50 cycles at 100 mA·g^(−1)within capacity retention of 82.58%but also deliver a relatively high reversible specific capacity of 518.24,445.52,418.18,345.33,and 278.05 mAh·g^(−1)at step-increased current density of 0.1,0.2,0.5,1.0,and 2.0 A·g^(−1),respectively.Therefore,the preparation process of the Cu6Sn5/CNTs-0.2 alloy thin-film electrode with improved electrochemical performance may provide a cost-effective strategy for the resource utilization of WPCBs to fabricate anode materials for lithium-ion batteries.展开更多
基金supported by the National Natural Science Foundation of China(Nos.52274292 and 51874046)the Outstanding Youth Foundation of Hubei Province,China(No.2020CFA090)the Young Topnotch Talent Cultivation Program of Hubei Province,China.
文摘Tin-based materials are very attractive anodes because of their high theoretical capacity,but their rapid capacity fading from volume expansions limits their practical applications during alloying and dealloying processes.Herein,the improved binder-free tin-copper intermetallic/carbon nanotubes(Cu6Sn5/CNTs)alloy thin-film electrodes are directly fabricated through efficient in situ electrodeposition from the leaching solution of treated waste-printed circuit boards(WPCBs).The characterization results show that the easily agglomerated Cu6Sn5 alloy nanoparticles are uniformly dispersed across the three-dimensional network when the CNTs concentration in the electrodeposition solution is maintained at 0.2 g·L−1.Moreover,the optimal Cu6Sn5/CNTs-0.2 alloy thin-film electrode can not only provide a decent discharge specific capacity of 458.35 mAh·g^(−1)after 50 cycles at 100 mA·g^(−1)within capacity retention of 82.58%but also deliver a relatively high reversible specific capacity of 518.24,445.52,418.18,345.33,and 278.05 mAh·g^(−1)at step-increased current density of 0.1,0.2,0.5,1.0,and 2.0 A·g^(−1),respectively.Therefore,the preparation process of the Cu6Sn5/CNTs-0.2 alloy thin-film electrode with improved electrochemical performance may provide a cost-effective strategy for the resource utilization of WPCBs to fabricate anode materials for lithium-ion batteries.