Critical cooling rate to avoid carbide precipitation during quenching of austenitic manganese steel was investigated by means of optical microscopy,image analyzer and numerical analysis.An efficient heat treatment ana...Critical cooling rate to avoid carbide precipitation during quenching of austenitic manganese steel was investigated by means of optical microscopy,image analyzer and numerical analysis.An efficient heat treatment analysis program including temperature-dependent material properties was developed for the prediction of cooling rate and probability of carbide precipitation during quenching by finite difference method.Time-dependent heat transfer coefficient was adopted to achieve more precise results.Area ratio of carbide precipitation was measured by image analyzer to determine the critical point of carbide precipitation.Temperature-dependent critical cooling rate at that point was calculated by the developed numerical program.Finally,the probability of carbide precipitation on the whole area of specimen can be predicted by the proposed numerical program and the numerical result of a specimen was compared with the experimental result.展开更多
In this study, residual stresses in heat treated specimen were measured by using ESPI (Electronic Speckle-Pattern Interferometry) combined with the hole-drilling method.The specimen, made of SUS 304 austenitic stainle...In this study, residual stresses in heat treated specimen were measured by using ESPI (Electronic Speckle-Pattern Interferometry) combined with the hole-drilling method.The specimen, made of SUS 304 austenitic stainless steel, was quenched and water cooled to room temperature.Numerical simulation using a hybrid FDM/FEM package was also carried out to simulate the heat treatment process.As a result, the thermal stress fields were obtained from both the experiment and the numerical simulation.By comparision of stress fields, results from the experimental method and numerical simulation well agreed to each other, therefore, it is proved that the presented experimental method is applicable and reliable for heat treatment induced residual stress measurement.展开更多
Shrinkage cavity may be detrimental to mechanical performances of casting parts.As a consequence,design engineers often use overly large safety factors in many designs due to insufficient understanding of quantitative...Shrinkage cavity may be detrimental to mechanical performances of casting parts.As a consequence,design engineers often use overly large safety factors in many designs due to insufficient understanding of quantitative effects of shrinkage cavity defects.In this paper,process of Al alloy wheel impact test was computationally analyzed for both the wheel models with and without shrinkage cavity defects.Based on shrinkage cavity data obtained from industrial CT (Computerized Tomography),the shrinkage cavity defects were modeled with SSM (Shape Simplification Method),which reconstructs shrinkage cavity defects to hollow spheroid primitives.After the impact simulation was conducted,the results show that under impact test condition,the wheel considering shrinkage cavity defects may fracture while the sound-assumed wheel may not.展开更多
It is important to analyse the casting product and the mold at the same time considering thermal contraction of the casting and thermal expansion of the mold. The analysis considering contact of the casting and the mo...It is important to analyse the casting product and the mold at the same time considering thermal contraction of the casting and thermal expansion of the mold. The analysis considering contact of the casting and the mold induces the precise prediction of stress distribution and the defect such as hot tearing. But it is difficult to generate FEM mesh for the interface of the casting and the mold. Moreover the mesh for the mold domain spends lots of computational time and memory for the analysis due to a number of meshes. Consequently we proposed the virtual mold technique which only uses mesh of the casting part for thermal stress analysis in casting process. The spring bar element in virtual mold technique is used to consider the contact of the casting and the mold. In general, a volume of the mold is much bigger than that of casting part, so the proposed technique decreases the number of mesh and saves the computational memory and time greatly. In this study, the proposed technique was verified by the comparison with the traditional contact technique on a specimen. And the proposed technique gave satisfactory results.展开更多
文摘Critical cooling rate to avoid carbide precipitation during quenching of austenitic manganese steel was investigated by means of optical microscopy,image analyzer and numerical analysis.An efficient heat treatment analysis program including temperature-dependent material properties was developed for the prediction of cooling rate and probability of carbide precipitation during quenching by finite difference method.Time-dependent heat transfer coefficient was adopted to achieve more precise results.Area ratio of carbide precipitation was measured by image analyzer to determine the critical point of carbide precipitation.Temperature-dependent critical cooling rate at that point was calculated by the developed numerical program.Finally,the probability of carbide precipitation on the whole area of specimen can be predicted by the proposed numerical program and the numerical result of a specimen was compared with the experimental result.
文摘In this study, residual stresses in heat treated specimen were measured by using ESPI (Electronic Speckle-Pattern Interferometry) combined with the hole-drilling method.The specimen, made of SUS 304 austenitic stainless steel, was quenched and water cooled to room temperature.Numerical simulation using a hybrid FDM/FEM package was also carried out to simulate the heat treatment process.As a result, the thermal stress fields were obtained from both the experiment and the numerical simulation.By comparision of stress fields, results from the experimental method and numerical simulation well agreed to each other, therefore, it is proved that the presented experimental method is applicable and reliable for heat treatment induced residual stress measurement.
文摘Shrinkage cavity may be detrimental to mechanical performances of casting parts.As a consequence,design engineers often use overly large safety factors in many designs due to insufficient understanding of quantitative effects of shrinkage cavity defects.In this paper,process of Al alloy wheel impact test was computationally analyzed for both the wheel models with and without shrinkage cavity defects.Based on shrinkage cavity data obtained from industrial CT (Computerized Tomography),the shrinkage cavity defects were modeled with SSM (Shape Simplification Method),which reconstructs shrinkage cavity defects to hollow spheroid primitives.After the impact simulation was conducted,the results show that under impact test condition,the wheel considering shrinkage cavity defects may fracture while the sound-assumed wheel may not.
文摘It is important to analyse the casting product and the mold at the same time considering thermal contraction of the casting and thermal expansion of the mold. The analysis considering contact of the casting and the mold induces the precise prediction of stress distribution and the defect such as hot tearing. But it is difficult to generate FEM mesh for the interface of the casting and the mold. Moreover the mesh for the mold domain spends lots of computational time and memory for the analysis due to a number of meshes. Consequently we proposed the virtual mold technique which only uses mesh of the casting part for thermal stress analysis in casting process. The spring bar element in virtual mold technique is used to consider the contact of the casting and the mold. In general, a volume of the mold is much bigger than that of casting part, so the proposed technique decreases the number of mesh and saves the computational memory and time greatly. In this study, the proposed technique was verified by the comparison with the traditional contact technique on a specimen. And the proposed technique gave satisfactory results.