Growth process of the NaY zeolite membranes was investigated by fluoride-containing precursor synthesis gel.Compared with the fluoride-free precursor synthesis gel,the irregular NaY zeolite crystals were dissolved int...Growth process of the NaY zeolite membranes was investigated by fluoride-containing precursor synthesis gel.Compared with the fluoride-free precursor synthesis gel,the irregular NaY zeolite crystals were dissolved into amorphous by the fluoride-containing precursor synthesis gel initially,the amorphous contained the Y-type zeolite characteristic bands by the IR characterization.The fine square NaY zeolite crystals arose from the amorphous,which were accumulated and gradually grew into a dense NaY zeolite layer on the support surface after 6.5 h.Because the excessive NaY zeolites were dissolved by the strong alkaline and fluoride-containing precursor synthesis gel,there was plenty of amorphous on NaY zeolites layer for prolonging the crystallization time.The assynthesized NaY zeolite membranes had a good separation performance and repeatability for separation of 10 wt%methanol(MeOH)/methyl methacrylate(MMA) mixture by pervaporation,the flux and separation factor were(1.27 ± 0.07) kg·M^(-2)·h^(-1) and(4900 ± 1500) at 323 K,respectively.Besides,the NaY zeolite membranes were applied to separate the other short chain alcohol from the various alcohol/organic ester and alcohol/organic ether mixtures,the NaY zeolite membranes showed high short chain alcohol perm-selectivity.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 21868012 and 21968009)Jiangxi Provincial Department of Science and Technology (20171BCB24005, 20181ACH80003, 20192ACB80003 and 20192BBH80024)。
文摘Growth process of the NaY zeolite membranes was investigated by fluoride-containing precursor synthesis gel.Compared with the fluoride-free precursor synthesis gel,the irregular NaY zeolite crystals were dissolved into amorphous by the fluoride-containing precursor synthesis gel initially,the amorphous contained the Y-type zeolite characteristic bands by the IR characterization.The fine square NaY zeolite crystals arose from the amorphous,which were accumulated and gradually grew into a dense NaY zeolite layer on the support surface after 6.5 h.Because the excessive NaY zeolites were dissolved by the strong alkaline and fluoride-containing precursor synthesis gel,there was plenty of amorphous on NaY zeolites layer for prolonging the crystallization time.The assynthesized NaY zeolite membranes had a good separation performance and repeatability for separation of 10 wt%methanol(MeOH)/methyl methacrylate(MMA) mixture by pervaporation,the flux and separation factor were(1.27 ± 0.07) kg·M^(-2)·h^(-1) and(4900 ± 1500) at 323 K,respectively.Besides,the NaY zeolite membranes were applied to separate the other short chain alcohol from the various alcohol/organic ester and alcohol/organic ether mixtures,the NaY zeolite membranes showed high short chain alcohol perm-selectivity.