The corrosion properties of pure zirconium(Zr)with different grain sizes in acid,alkali,and salt environments were studied.The microstructures of pure Zr were observed by optical microscope,X-ray diffractometer,and el...The corrosion properties of pure zirconium(Zr)with different grain sizes in acid,alkali,and salt environments were studied.The microstructures of pure Zr were observed by optical microscope,X-ray diffractometer,and electron backscattered diffraction probe.The corrosion resistance of pure Zr was analyzed by electrochemical corrosion test and immersion test.Results show that pure Zr with grain size of 4–32μm can be obtained after annealing at 800°C for different durations,and the relationship between grain size and annealing duration is D^(3)−D_(0)^(3)=3.35t.The electrochemical corrosion and immersion corrosion test results show that the pure Zr with grain size of about 24μm(annealing at 800°C for 20 h)possesses the optimal corrosion resistance.展开更多
基金National Natural Science Foundation of China(52071126)Natural Science Foundation of Tianjin City,China(22JCQNJC01240)+2 种基金Central Guidance on Local Science and Technology Development Fund of Hebei Province(226Z1009G)Special Funds for Science and Technology Innovation in Hebei(2022X19)Foundation Strengthening Program(2019-JCJQ-00)。
文摘The corrosion properties of pure zirconium(Zr)with different grain sizes in acid,alkali,and salt environments were studied.The microstructures of pure Zr were observed by optical microscope,X-ray diffractometer,and electron backscattered diffraction probe.The corrosion resistance of pure Zr was analyzed by electrochemical corrosion test and immersion test.Results show that pure Zr with grain size of 4–32μm can be obtained after annealing at 800°C for different durations,and the relationship between grain size and annealing duration is D^(3)−D_(0)^(3)=3.35t.The electrochemical corrosion and immersion corrosion test results show that the pure Zr with grain size of about 24μm(annealing at 800°C for 20 h)possesses the optimal corrosion resistance.