The resistive switching memory characteristics of 100 randomly measured devices were observed by reducing device size in a Cr/Cr Ox/Ti Ox/Ti N structure for the first time.Transmission electron microscope image confir...The resistive switching memory characteristics of 100 randomly measured devices were observed by reducing device size in a Cr/Cr Ox/Ti Ox/Ti N structure for the first time.Transmission electron microscope image confirmed a viahole size of 0.4 lm.A 3-nm-thick amorphous Ti Oxwith 4-nm-thick polycrystalline Cr Oxlayer was observed.A small 0.4-lm device shows reversible resistive switching at a current compliance of 300 l A as compared to other larger size devices(1–8 lm)owing to reduction of leakage current through the Ti Oxlayer.Good device-to-device uniformity with a yield of[85%has been clarified by weibull distribution owing to higher slope/shape factor.The switching mechanism is based on oxygen vacancy migration from the Cr Oxlayer and filament formation/rupture in the Ti Oxlayer.Long read pulse endurance of[105cycles,good data retention of 6 h,and a program/erase speed of 1 ls pulse width have been obtained.展开更多
基金supported by Ministry of Sci ence and Technology(MOST)Taiwan,under Contract no.NSC-1022221-E-182-057-MY2grateful to EOL/ITRI Hsinchu,Taiwan for their experimental support
文摘The resistive switching memory characteristics of 100 randomly measured devices were observed by reducing device size in a Cr/Cr Ox/Ti Ox/Ti N structure for the first time.Transmission electron microscope image confirmed a viahole size of 0.4 lm.A 3-nm-thick amorphous Ti Oxwith 4-nm-thick polycrystalline Cr Oxlayer was observed.A small 0.4-lm device shows reversible resistive switching at a current compliance of 300 l A as compared to other larger size devices(1–8 lm)owing to reduction of leakage current through the Ti Oxlayer.Good device-to-device uniformity with a yield of[85%has been clarified by weibull distribution owing to higher slope/shape factor.The switching mechanism is based on oxygen vacancy migration from the Cr Oxlayer and filament formation/rupture in the Ti Oxlayer.Long read pulse endurance of[105cycles,good data retention of 6 h,and a program/erase speed of 1 ls pulse width have been obtained.