Enhanced charge separation by interchain hole delocalization in nonfullerene acceptor-based bulk heterojunction materials

Bulk heterojunction(BHJ)composites show improved power conversion efficiencies when optimized in terms of morphology using various film processing methods.A reduced carrier recombination loss in an optimized BHJ was characterized previously.However,the driving force that leads to this reduction was not clearly understood.In this study,we focus on the decreased carrier recombination loss and its driving force in optimized nonfullerene acceptor-based PTB7-Th:IEICO-4F BHJ composites.We demonstrate that the optimized BHJ shows deactivation in the sub-nanosecond nongeminate carrier recombination process.The driving force for this deactivation was determined to be the improved interchain hole delocalization between the polymers.An enhanced interchain hole delocalization was observed using steady-state photoinduced absorption(PIA)spectroscopy.In particular,increased splitting between the polaron PIA bands was noted.Moreover,improved interchain hole delocalization was observed for other state-of-the-art BHJ materials,including D18:Y6 with optimized morphologies.

Non-Fullerene-Based Inverted Organic Photovoltaic Device with Long-Term Stability

In this work,we developed the PM6:Y6-based inverted structure organic photovoltaic(i-OPV)with improved power conversion efficiency(PCE)and long-term stability by resolving the origins of the performance deterioration.The deep defects between the metal oxide-based electron transport layer and bulk-heterojunction photoactive layer interface were responsible for suboptimal PCE and facilitated degradation of devices.While the density of deep traps is increased during the storage of i-OPV,the penetrative oxygen-containing defects additionally generated shallow traps below the band-edge of Y6,causing an additional loss in the open-circuit voltage.The suppression of interfacial defects by chemical modification effectively improved the PCE and long-term stability of i-OPV.The modified i-OPV(mi-OPV)achieved a PCE of 17.42%,which is the highest value among the reported PM6:Y6-based i-OPV devices.Moreover,long-term stability was significantly improved:~90%and~80%retention of its initial PCE after 1200 h of air storage and illumination,respectively.