Plasma Surface Functionalization of Biaxially Oriented Polypropylene Films with Trimethyl Borate
1
作者 Nursel Dilsiz Hande Yavuz +1 位作者 suleyman corekci Mehmet Cakmak 《Advances in Materials Physics and Chemistry》 2011年第2期50-55,共6页
The radiofrequency plasma (13.56 MHz) was employed to polymerize trimethyl borate (TMB) monomer/N2 gas mixture on the surface of biaxially oriented polypropylene (BOPP) films. Plasma polymer coated polypropylene films... The radiofrequency plasma (13.56 MHz) was employed to polymerize trimethyl borate (TMB) monomer/N2 gas mixture on the surface of biaxially oriented polypropylene (BOPP) films. Plasma polymer coated polypropylene films were examined by flame retardancy test (limiting oxygen index, LOI). The highest LOI value calculated for the untreated BOPP sample was 18.4 (v/v O2%) and 24.2 (v/v O2%) for the 55 W 30 minutes treated sample. The plasma polymers were characterized by FTIR spectroscopy and AFM. According to the FTIR results, the -OH, B-CH3, B-O, and BH2 functional groups were detected. It was found that the highest surface roughness belonged to 40 W 30 min treated BOPP sample which was calculated as 9.78 nm (10 μm × 10 μm). Moreover, the wettability of the modified BOPP film surfaces was characterized via contact angle measurements. The water contact angle values have decreased from 109.6? to the lowest value of 68.2? after the plasma treatment. The results showed that TMB/N2 plasma modification could be used as an alternative method for the enhancement of flame retardancy and hydrophilicity of BOPP film. 展开更多
关键词 Polypropylene Film Trimethyl Borate Plasma Treatment Flame Retardancy HYDROPHILICITY
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部