The microstructures of Al-Zn-Mg-Cu-Zr al- loys with minor Sc were studied by using optical microscope（OM）, scanning electron microscope （SEM） and transmission electron microscope（TEM）. The tensile mechanical pro...The microstructures of Al-Zn-Mg-Cu-Zr al- loys with minor Sc were studied by using optical microscope（OM）, scanning electron microscope （SEM） and transmission electron microscope（TEM）. The tensile mechanical properties and electric conductivity of the studied alloys under different treatment conditions were tested. The results show that adding minor Sc can greatly fines the grain size of the Al-Zn-Mg-Cu-Zr alloy ingots and obviously improves the tensile properties and electric conductivity of the alloys. The strengthening mechanism is considered as fine grain strengthening, sub-structure strengthening and dispersion strengthening by Al3 （Sc, Zr）.展开更多
A new type of aluminum lithium alloy （Al–Li alloy） Al–Li–S–4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti–...A new type of aluminum lithium alloy （Al–Li alloy） Al–Li–S–4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti–6Al–4V alloy （Ti alloy） strap by FM 94 film adhesive after the surface was treated. Fatigue crack growth of samples was investigated under cyclic loading with stress ratio （R） of 0.1 and load amplitude constant. The results show that Al–Li alloy plate bonded with Ti alloy strap could retard fatigue crack propagation. Retardation effect is related with width and thickness of strap. Flaws have an observable effect on crack propagation direction.展开更多
文摘The microstructures of Al-Zn-Mg-Cu-Zr al- loys with minor Sc were studied by using optical microscope（OM）, scanning electron microscope （SEM） and transmission electron microscope（TEM）. The tensile mechanical properties and electric conductivity of the studied alloys under different treatment conditions were tested. The results show that adding minor Sc can greatly fines the grain size of the Al-Zn-Mg-Cu-Zr alloy ingots and obviously improves the tensile properties and electric conductivity of the alloys. The strengthening mechanism is considered as fine grain strengthening, sub-structure strengthening and dispersion strengthening by Al3 （Sc, Zr）.
文摘A new type of aluminum lithium alloy （Al–Li alloy） Al–Li–S–4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti–6Al–4V alloy （Ti alloy） strap by FM 94 film adhesive after the surface was treated. Fatigue crack growth of samples was investigated under cyclic loading with stress ratio （R） of 0.1 and load amplitude constant. The results show that Al–Li alloy plate bonded with Ti alloy strap could retard fatigue crack propagation. Retardation effect is related with width and thickness of strap. Flaws have an observable effect on crack propagation direction.