Magnesium and its alloys are ideal candidates for bioabsorbable implants.However,they can dissolve too rapidly in the human body for most applications.In this research,high purified magnesium(HP-Mg)was coated with ste...Magnesium and its alloys are ideal candidates for bioabsorbable implants.However,they can dissolve too rapidly in the human body for most applications.In this research,high purified magnesium(HP-Mg)was coated with stearic acid(SA)to slow the corrosion rate of magnesium in simulated body fluid at 37±1°C.HP-Mg was anodized(AC and DC voltages)to form an oxide/hydroxide layer,and then it was immersed in a SA solution.The SA coated layer surface,anodized layer,and the thickness of the oxide/hydroxide layer were investigated with Scanning Electron Microscopy(SEM).Electrochemical impedance spectroscopy(EIS)and potentiodynamic polarization(PDP)were used to estimate the corrosion rate of HP-Mg specimens.The results confirm that the hydrophobic coating can decrease the corrosion rate of HP-Mg by more than 1000x.The protectiveness of coated layer for anodized specimens with AC voltage continue for 2 and 3 weeks.For the HP-Mg coated anodized with DC voltage,the coated layer could improve the corrosion resistance for only a few days.展开更多
文摘Magnesium and its alloys are ideal candidates for bioabsorbable implants.However,they can dissolve too rapidly in the human body for most applications.In this research,high purified magnesium(HP-Mg)was coated with stearic acid(SA)to slow the corrosion rate of magnesium in simulated body fluid at 37±1°C.HP-Mg was anodized(AC and DC voltages)to form an oxide/hydroxide layer,and then it was immersed in a SA solution.The SA coated layer surface,anodized layer,and the thickness of the oxide/hydroxide layer were investigated with Scanning Electron Microscopy(SEM).Electrochemical impedance spectroscopy(EIS)and potentiodynamic polarization(PDP)were used to estimate the corrosion rate of HP-Mg specimens.The results confirm that the hydrophobic coating can decrease the corrosion rate of HP-Mg by more than 1000x.The protectiveness of coated layer for anodized specimens with AC voltage continue for 2 and 3 weeks.For the HP-Mg coated anodized with DC voltage,the coated layer could improve the corrosion resistance for only a few days.