Compressive stress and tensile stress were applied to concrete specimens using test rigs designed by RILEM TC 246-TDC. Ultrasonic wave velocity and autoclam permeability system were used to characterize the damage var...Compressive stress and tensile stress were applied to concrete specimens using test rigs designed by RILEM TC 246-TDC. Ultrasonic wave velocity and autoclam permeability system were used to characterize the damage variable and gas permeability coefficient of concrete, respectively. The experimental results show that the strain value of concrete increases with the increasing of stress level and loading time. The damage variable and gas permeability coefficient of concrete under compressive stress decrease at first and increase after a threshold value between 0 and 0.6. When the concrete is under tensile load, the damage variable and gas permeability coefficient increase with tensile stress, with a significant increase from 0.3 to 0.6 tensile stress. There is a strong linear relationship between the damage variable and the gas permeability coefficient, suggesting both as good indicators to characterize the damage of concrete under stress.展开更多
基金Funded by the National Natural Science Foundation of China(No.51320105016)
文摘Compressive stress and tensile stress were applied to concrete specimens using test rigs designed by RILEM TC 246-TDC. Ultrasonic wave velocity and autoclam permeability system were used to characterize the damage variable and gas permeability coefficient of concrete, respectively. The experimental results show that the strain value of concrete increases with the increasing of stress level and loading time. The damage variable and gas permeability coefficient of concrete under compressive stress decrease at first and increase after a threshold value between 0 and 0.6. When the concrete is under tensile load, the damage variable and gas permeability coefficient increase with tensile stress, with a significant increase from 0.3 to 0.6 tensile stress. There is a strong linear relationship between the damage variable and the gas permeability coefficient, suggesting both as good indicators to characterize the damage of concrete under stress.