The shrinkage and chilling tendency of spheroidal graphite (abbreviated SG) cast iron is much greater than that of the flake graphite cast iron in spite of its higher amount of C and Si contents. Why? The main reason ...The shrinkage and chilling tendency of spheroidal graphite (abbreviated SG) cast iron is much greater than that of the flake graphite cast iron in spite of its higher amount of C and Si contents. Why? The main reason should be the difference in their graphitization during the eutectic solidification. In this paper, we discuss the difference in the solidification mechanism of both cast irons for solving these problems using unidirectional solidification and the cooling curves of the spheroidal graphite cast iron. The eutectic solidification rate of the SG cast iron is controlled by the diffusion of carbon through the austenite shell, and the final thickness is 1.4 times the radius of the SG, therefore, the reduction of the SG size, namely, the increase in the number, is the main solution of these problems.展开更多
The thirteen mother alloys,C%+1/3Si%=4.45%,differing in their Si,Ce,Sb and Sn contents,were prepared.Seventy grams of these alloys was remelted in a high purity alumina crucible at 1,450oC under an Ar atmosphere,and t...The thirteen mother alloys,C%+1/3Si%=4.45%,differing in their Si,Ce,Sb and Sn contents,were prepared.Seventy grams of these alloys was remelted in a high purity alumina crucible at 1,450oC under an Ar atmosphere,and then cooled at 30 K/min for obtaining their cooling curves.Their graphite morphologies were observed using an optical microscope and an SEM.Their three-dimensional graphite shapes were observed by the SEM using the samples whose matrices were etched off with an acid-aqua solution,to confirm the chunky graphite.For discussing the influence of the Si and Ce contents on the chunky graphite formation,two experiments were carried out.In the first one,the Si contents were changed from 0 to 4% in the 0.15%Ce alloys,and for the second one,the 3.5%Si and 4%Si samples that differed in the Ce contents of 0.1 and 0.2% were used.In the third experiment,the influence of Sb and Sn on the chunky graphite formation was investigated by using the 4%Si and 0.1%Ce samples.The results showed that with the increase of the Si content,the volume fraction of the chunky graphite increases,while the volume fraction of the ledeburite decreases,and the chunky graphite volume fraction in the 0.2%Ce samples is higher than that of the 0.1%Ce samples.The effect of the Sb and Sn additions on the prevention of chunky graphite formation cannot be confirmed due to their high Si contents.Therefore,further studies will be needed in this field.展开更多
文摘The shrinkage and chilling tendency of spheroidal graphite (abbreviated SG) cast iron is much greater than that of the flake graphite cast iron in spite of its higher amount of C and Si contents. Why? The main reason should be the difference in their graphitization during the eutectic solidification. In this paper, we discuss the difference in the solidification mechanism of both cast irons for solving these problems using unidirectional solidification and the cooling curves of the spheroidal graphite cast iron. The eutectic solidification rate of the SG cast iron is controlled by the diffusion of carbon through the austenite shell, and the final thickness is 1.4 times the radius of the SG, therefore, the reduction of the SG size, namely, the increase in the number, is the main solution of these problems.
文摘The thirteen mother alloys,C%+1/3Si%=4.45%,differing in their Si,Ce,Sb and Sn contents,were prepared.Seventy grams of these alloys was remelted in a high purity alumina crucible at 1,450oC under an Ar atmosphere,and then cooled at 30 K/min for obtaining their cooling curves.Their graphite morphologies were observed using an optical microscope and an SEM.Their three-dimensional graphite shapes were observed by the SEM using the samples whose matrices were etched off with an acid-aqua solution,to confirm the chunky graphite.For discussing the influence of the Si and Ce contents on the chunky graphite formation,two experiments were carried out.In the first one,the Si contents were changed from 0 to 4% in the 0.15%Ce alloys,and for the second one,the 3.5%Si and 4%Si samples that differed in the Ce contents of 0.1 and 0.2% were used.In the third experiment,the influence of Sb and Sn on the chunky graphite formation was investigated by using the 4%Si and 0.1%Ce samples.The results showed that with the increase of the Si content,the volume fraction of the chunky graphite increases,while the volume fraction of the ledeburite decreases,and the chunky graphite volume fraction in the 0.2%Ce samples is higher than that of the 0.1%Ce samples.The effect of the Sb and Sn additions on the prevention of chunky graphite formation cannot be confirmed due to their high Si contents.Therefore,further studies will be needed in this field.