(GdCa)(SiO)Oapatite crystals doped with different concentrations of Ce were synthesized by the Floating Zone(FZ) method, and we have evaluated the photoluminescence(PL) and radio luminescence(RL) properties. In PL, an...(GdCa)(SiO)Oapatite crystals doped with different concentrations of Ce were synthesized by the Floating Zone(FZ) method, and we have evaluated the photoluminescence(PL) and radio luminescence(RL) properties. In PL, an emission band appeared around 400 nm under excitation at 300 nm due to the5 d-4 f transitions of Ce3+. The PL decay curves were approximated by a second-order exponential decay function, and the derived decay time constants ranged around 20-25 ns and 40-480 ns. Similar emission was observed in RL, but the decay time constants were much longer than those in PL. The RL afterglow was the lowest in the 1.0% Ce-doped sample. The 1.0% and 2.0% Ce-doped samples showed a full-energy peak in the pulse height spectrum measured underAm 5.5 MeV α-ray irradiation, and the absolute scintillation light yields were estimated to be around 55 and 36 ph/5.5 MeV-a, respectively.展开更多
基金Project supported by a Grant-in-Aid for Scientific Research(A) 26249147 from the Ministry of Education,Culture,Sports,Science and Technology of Japan(MEXT)JST A-step,Cooperative Research Project of Research Institute of Electronics,Shizuoka University+1 种基金Inamori FoundationKRF Foundation
文摘(GdCa)(SiO)Oapatite crystals doped with different concentrations of Ce were synthesized by the Floating Zone(FZ) method, and we have evaluated the photoluminescence(PL) and radio luminescence(RL) properties. In PL, an emission band appeared around 400 nm under excitation at 300 nm due to the5 d-4 f transitions of Ce3+. The PL decay curves were approximated by a second-order exponential decay function, and the derived decay time constants ranged around 20-25 ns and 40-480 ns. Similar emission was observed in RL, but the decay time constants were much longer than those in PL. The RL afterglow was the lowest in the 1.0% Ce-doped sample. The 1.0% and 2.0% Ce-doped samples showed a full-energy peak in the pulse height spectrum measured underAm 5.5 MeV α-ray irradiation, and the absolute scintillation light yields were estimated to be around 55 and 36 ph/5.5 MeV-a, respectively.