The microwave induced argon plasma was applied to the preparation of NaOH-activated carbon from sugar cane bagasse. The distinguished feature of the heating technique with this cold plasma is the short operation time....The microwave induced argon plasma was applied to the preparation of NaOH-activated carbon from sugar cane bagasse. The distinguished feature of the heating technique with this cold plasma is the short operation time. The carbonization and the activation process were finalized in one step within 3 min. The prepared activated carbon with NaOH ratio 3 to bagasse characterized using N2 adsorption of type IV (IUPAC classification) to give specific surface area of 1980 m2/g and mesopore volume of 0.73 ml/g. It also showed a higher specific capacitance of 201 F/g in 1 M H2SO4 solution (with standard three electrodes) than the corresponding one by the conventional heating, previously reported. The other features were the absence of oxygen groups and the presence of carbon centered stable radicals, detected by ESR spectra, on the surface.展开更多
A direct regioselective preparation of 2-hydroxynaphthalene-6-carboxylic acid, a useful industrial intermediate of aro-matic polyester from 2-naphthol was conducted by use of excess amount of K2CO3 (10-fold molar to 2...A direct regioselective preparation of 2-hydroxynaphthalene-6-carboxylic acid, a useful industrial intermediate of aro-matic polyester from 2-naphthol was conducted by use of excess amount of K2CO3 (10-fold molar to 2-naphthol) under supercritical CO2 at 10 MPa and 473 K. The obtained yield under this condition was ca. 20 mol% to 2-naphthol. The further investigations may provide an alternative process to the conventional Kolbe-Schmitt reaction, because of no use of strong alkali and recoverability of K2CO3. Theoretical explanation about the regioselectivity was achieved by means of DFT calculations.展开更多
Methane was decomposed to hydrogen and carbon nanotubes (CNTs) by microwave plasma, using Fe/Si catalyst activated by biased (—150 V) hydrogen plasma for various treatment times. Upon exposure to biased hydrogen plas...Methane was decomposed to hydrogen and carbon nanotubes (CNTs) by microwave plasma, using Fe/Si catalyst activated by biased (—150 V) hydrogen plasma for various treatment times. Upon exposure to biased hydrogen plasma, the catalyst surface becomes lumpy within 1 min, coheres between 5 and 10 min and forms particles after 20 min. The methane conversion increased up to 93% over the treatment time of 5 min. The hydrogen yield showed as similar tendency as the methane conversion and kept 83% at treatment time of 5 min. The treatment time up to 1 min increased the amount of deposited carbon, and after treatment time of 5 min it dropped;then again after treatment time of 20 min, it increased to reach a maximum value of 22 gc/gcat. Deposited carbon was found to be consisted of carbon nanotubes. It grew vertically on the catalyst surface and reached a maximum length of 30.7 nm after treatment time of 10 min. Multiple types of CNTs were present, and the CNT diameters decreased with increasing plasma treatment time.展开更多
Biomass conversion by plasma has the advantage of mainly producing gaseous products, H2, CO and CO2. Though the thermal plasma has been used for this conversion, the plasma temperature is too high to be unfit for the ...Biomass conversion by plasma has the advantage of mainly producing gaseous products, H2, CO and CO2. Though the thermal plasma has been used for this conversion, the plasma temperature is too high to be unfit for the conversion biomass. The temperature of cold plasma, however, is lower under 3000 K. It expects to be adequate for biomass conversion. Cold plasma can be obtained with irradiation microwave (2.45 GHz) or radio frequency (13.5 MHz) under reduce gas pressure. Therefore, in present study, the effective decomposition of cellulose by microwave plasma (MWP) and radio frequency plasma (RFP) is examined. The conversion of cellulose by MWP (XMWP) is higher than that by RFP (XRFP), irrespective of the reaction time. XMWP and XRFP reach 92.8 wt% at 10 min and 68.1 wt% at 30 min. The maximum yield of gaseous products (Ygas) by MWP is 85.1 wt% at 10 min, higher by 23.2 wt% than Ygas by RFP at 30 min. The amount of H2 and CO obtained by MWP is 18.0 mmol/g and 23.5 mmol/g, it is larger than that obtained by RFP. Comparing the relationship between conversion and yield, Ygas of MWP is slightly higher than that of RFP under X of 60 wt%, and both Ygas is almost same over 60 wt%. The amount of H2 and CO obtained by MWP is larger by 9.3 mmol/g and 9.6 mmol/g than that obtained by RFP. C, H and O element in cellulose is mainly distributed to H2 and CO by MWP. RFP mainly distributes H and O element to the other gases without H2 and CO. In addition, a large amount of C element is remains in the residue. Those results is found that MWP was more suitable for cellulose gasification than RFP, since MWP can highly convert C, H and O element to H2 and CO by higher energy of microwave frequency in comparison with radio frequency.展开更多
文摘The microwave induced argon plasma was applied to the preparation of NaOH-activated carbon from sugar cane bagasse. The distinguished feature of the heating technique with this cold plasma is the short operation time. The carbonization and the activation process were finalized in one step within 3 min. The prepared activated carbon with NaOH ratio 3 to bagasse characterized using N2 adsorption of type IV (IUPAC classification) to give specific surface area of 1980 m2/g and mesopore volume of 0.73 ml/g. It also showed a higher specific capacitance of 201 F/g in 1 M H2SO4 solution (with standard three electrodes) than the corresponding one by the conventional heating, previously reported. The other features were the absence of oxygen groups and the presence of carbon centered stable radicals, detected by ESR spectra, on the surface.
文摘A direct regioselective preparation of 2-hydroxynaphthalene-6-carboxylic acid, a useful industrial intermediate of aro-matic polyester from 2-naphthol was conducted by use of excess amount of K2CO3 (10-fold molar to 2-naphthol) under supercritical CO2 at 10 MPa and 473 K. The obtained yield under this condition was ca. 20 mol% to 2-naphthol. The further investigations may provide an alternative process to the conventional Kolbe-Schmitt reaction, because of no use of strong alkali and recoverability of K2CO3. Theoretical explanation about the regioselectivity was achieved by means of DFT calculations.
文摘Methane was decomposed to hydrogen and carbon nanotubes (CNTs) by microwave plasma, using Fe/Si catalyst activated by biased (—150 V) hydrogen plasma for various treatment times. Upon exposure to biased hydrogen plasma, the catalyst surface becomes lumpy within 1 min, coheres between 5 and 10 min and forms particles after 20 min. The methane conversion increased up to 93% over the treatment time of 5 min. The hydrogen yield showed as similar tendency as the methane conversion and kept 83% at treatment time of 5 min. The treatment time up to 1 min increased the amount of deposited carbon, and after treatment time of 5 min it dropped;then again after treatment time of 20 min, it increased to reach a maximum value of 22 gc/gcat. Deposited carbon was found to be consisted of carbon nanotubes. It grew vertically on the catalyst surface and reached a maximum length of 30.7 nm after treatment time of 10 min. Multiple types of CNTs were present, and the CNT diameters decreased with increasing plasma treatment time.
文摘Biomass conversion by plasma has the advantage of mainly producing gaseous products, H2, CO and CO2. Though the thermal plasma has been used for this conversion, the plasma temperature is too high to be unfit for the conversion biomass. The temperature of cold plasma, however, is lower under 3000 K. It expects to be adequate for biomass conversion. Cold plasma can be obtained with irradiation microwave (2.45 GHz) or radio frequency (13.5 MHz) under reduce gas pressure. Therefore, in present study, the effective decomposition of cellulose by microwave plasma (MWP) and radio frequency plasma (RFP) is examined. The conversion of cellulose by MWP (XMWP) is higher than that by RFP (XRFP), irrespective of the reaction time. XMWP and XRFP reach 92.8 wt% at 10 min and 68.1 wt% at 30 min. The maximum yield of gaseous products (Ygas) by MWP is 85.1 wt% at 10 min, higher by 23.2 wt% than Ygas by RFP at 30 min. The amount of H2 and CO obtained by MWP is 18.0 mmol/g and 23.5 mmol/g, it is larger than that obtained by RFP. Comparing the relationship between conversion and yield, Ygas of MWP is slightly higher than that of RFP under X of 60 wt%, and both Ygas is almost same over 60 wt%. The amount of H2 and CO obtained by MWP is larger by 9.3 mmol/g and 9.6 mmol/g than that obtained by RFP. C, H and O element in cellulose is mainly distributed to H2 and CO by MWP. RFP mainly distributes H and O element to the other gases without H2 and CO. In addition, a large amount of C element is remains in the residue. Those results is found that MWP was more suitable for cellulose gasification than RFP, since MWP can highly convert C, H and O element to H2 and CO by higher energy of microwave frequency in comparison with radio frequency.