AA 6061 alloy and interstitial-free(IF)steel plates were joined by the friction stir welding(FSW)method,and the microstructure,mechanical properties,and biaxial stretch formability of the friction stir welded(FSWed)pa...AA 6061 alloy and interstitial-free(IF)steel plates were joined by the friction stir welding(FSW)method,and the microstructure,mechanical properties,and biaxial stretch formability of the friction stir welded(FSWed)parts were investigated.The results indicate that the FSWed parts showed optimum tensile strength during FSW with the 0.4-mm offset position of the tool.The Fe4Al13 intermetallic compound formed in the defect-free intersection of AA 6061 and IF-steel plates during FSW.The hardness of the IF-steel part of the FSWed region increased almost 90%relative to its initial hardness of HV0.2 105.The tensile and yield strengths of FSWed regions were approximately 170 MPa and 145 MPa,respectively.According to the formability tests,the Erichsen Index(EI)of the IF-steel,AA 6061,and the FSWed samples were determined to be 2.9 mm,1.9 mm,and 2.1 mm,respectively.The EI of the FSWed sample was almost the same as that of the AA 6061 alloy.However,it decreased compared with that of the IF-steel.The force at EI(FEI)was approximately 1180 N for the FSWed condition.This value is approximately 70%higher than that of AA 6061 alloy.展开更多
The aim of this work is to investigate the mechanical properties and microstructures of friction-stir welded(FSWed) St52 structural steel joints. In this study, St52 steel plates with a thickness of 4 mm were butt-wel...The aim of this work is to investigate the mechanical properties and microstructures of friction-stir welded(FSWed) St52 structural steel joints. In this study, St52 steel plates with a thickness of 4 mm were butt-welded by friction-stir welding(FSW) using a tungsten carbide tool having a conical pin. The microstructure of the welded zone consists of equiaxed fine ferrite, grain boundary ferrite, Widmanstatten ferrite, and aggregates of ferrite + cementite. The microhardness measurements showed that the hardness of the welded zone was significantly higher than that of the base metal. The FSWed St52 joint exhibited a significant strength overmatching in the weld region and a strength performance similar to or slightly higher than that of the base plate.展开更多
基金supported by “The World Academy of Sciences(TWAS)under the Visiting Researchers program of TWAS-UNESCO Associateship Scheme(No.3240290077)”
文摘AA 6061 alloy and interstitial-free(IF)steel plates were joined by the friction stir welding(FSW)method,and the microstructure,mechanical properties,and biaxial stretch formability of the friction stir welded(FSWed)parts were investigated.The results indicate that the FSWed parts showed optimum tensile strength during FSW with the 0.4-mm offset position of the tool.The Fe4Al13 intermetallic compound formed in the defect-free intersection of AA 6061 and IF-steel plates during FSW.The hardness of the IF-steel part of the FSWed region increased almost 90%relative to its initial hardness of HV0.2 105.The tensile and yield strengths of FSWed regions were approximately 170 MPa and 145 MPa,respectively.According to the formability tests,the Erichsen Index(EI)of the IF-steel,AA 6061,and the FSWed samples were determined to be 2.9 mm,1.9 mm,and 2.1 mm,respectively.The EI of the FSWed sample was almost the same as that of the AA 6061 alloy.However,it decreased compared with that of the IF-steel.The force at EI(FEI)was approximately 1180 N for the FSWed condition.This value is approximately 70%higher than that of AA 6061 alloy.
文摘The aim of this work is to investigate the mechanical properties and microstructures of friction-stir welded(FSWed) St52 structural steel joints. In this study, St52 steel plates with a thickness of 4 mm were butt-welded by friction-stir welding(FSW) using a tungsten carbide tool having a conical pin. The microstructure of the welded zone consists of equiaxed fine ferrite, grain boundary ferrite, Widmanstatten ferrite, and aggregates of ferrite + cementite. The microhardness measurements showed that the hardness of the welded zone was significantly higher than that of the base metal. The FSWed St52 joint exhibited a significant strength overmatching in the weld region and a strength performance similar to or slightly higher than that of the base plate.