Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were opt...Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were optimized by orthogonal tests.The PTA welding parameters including welding current,powder feed rate and welding speed have significant influence on the tungsten carbide degradation.The values for the optimum welding current,powder feed rate and welding speed were determined to be100A,25g/min and40mm/min,respectively.The produced WC/Ni-based composite coatings were crack-and degradation-free.The microstructure of deposited layers,as well as the microstructure and microhardness of the optimal coating were further analyzed.展开更多
基金Project (2016YFB0300502) supported by the National Key Research and Development Program of ChinaProjects (51601129,51775386) supported by the National Natural Science Foundation of China+2 种基金Project (16PJ1410000) supported by Shanghai Pujiang Program,ChinaProject (16ZR1438700) supported by the Natural Science Foundation of Shanghai,ChinaProject (TPL1706) supported by Traction Power State Key Laboratory of Southwest Jiaotong University,China
文摘Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were optimized by orthogonal tests.The PTA welding parameters including welding current,powder feed rate and welding speed have significant influence on the tungsten carbide degradation.The values for the optimum welding current,powder feed rate and welding speed were determined to be100A,25g/min and40mm/min,respectively.The produced WC/Ni-based composite coatings were crack-and degradation-free.The microstructure of deposited layers,as well as the microstructure and microhardness of the optimal coating were further analyzed.