Although using elemental powder mixtures may provide broad alloy selection at low cost for selective laser melting(SLM), there is still a concern on the resultant microstructural and chemical homogeneity of the produc...Although using elemental powder mixtures may provide broad alloy selection at low cost for selective laser melting(SLM), there is still a concern on the resultant microstructural and chemical homogeneity of the produced parts. Hence, this work investigates the microstructure and mechanical properties of a SLM-produced Ti-35 Nb composite(in wt%) using elemental powder. The microstructural characteristics including ? phase, undissolved Nb particles and chemical homogeneity were detailed investigated.Nanoindentation revealed the presence of relatively soft undissolved Nb particles and weak interface bonding around Nb-rich regions in as-SLMed samples. Solid-solution treatment can not only improve chemical homogeneity but also enhance bonding through grain boundary strengthening, resulting in43 % increase in tensile elongation for the heat-treated Ti-35 Nb compared to the as-SLMed counterpart. The analyses of tensile fractures and shear bands further confirmed the correlation between the different phases and the ductility of Ti-35 Nb. In particular, the weak bonding between undissolved Nb and the matrix in the as-SLMed sample reduces its ductility while the ? grains in solid-solution treated Ti-Nb alloy can induce a relatively stable plastic flow therefore better ductility. This work sheds insight into the understanding of homogenization of microstructure and phases of SLM-produced alloys from an elemental powder mixture.展开更多
基金support of the ECU Postgraduate Research AwardForrest Research Foundation Ph D Scholarship+1 种基金the Australian Government Research Training Program Scholarship(ECU)the facilities,and the scientific and technical assistance of the Australian Microscopy&Microanalysis Research Facility at the Centre for Microscopy,Characterisation&Analysis,The University of Western Australia,a facility funded by the University,State and Commonwealth Governments。
文摘Although using elemental powder mixtures may provide broad alloy selection at low cost for selective laser melting(SLM), there is still a concern on the resultant microstructural and chemical homogeneity of the produced parts. Hence, this work investigates the microstructure and mechanical properties of a SLM-produced Ti-35 Nb composite(in wt%) using elemental powder. The microstructural characteristics including ? phase, undissolved Nb particles and chemical homogeneity were detailed investigated.Nanoindentation revealed the presence of relatively soft undissolved Nb particles and weak interface bonding around Nb-rich regions in as-SLMed samples. Solid-solution treatment can not only improve chemical homogeneity but also enhance bonding through grain boundary strengthening, resulting in43 % increase in tensile elongation for the heat-treated Ti-35 Nb compared to the as-SLMed counterpart. The analyses of tensile fractures and shear bands further confirmed the correlation between the different phases and the ductility of Ti-35 Nb. In particular, the weak bonding between undissolved Nb and the matrix in the as-SLMed sample reduces its ductility while the ? grains in solid-solution treated Ti-Nb alloy can induce a relatively stable plastic flow therefore better ductility. This work sheds insight into the understanding of homogenization of microstructure and phases of SLM-produced alloys from an elemental powder mixture.
