Carbonate was added to the silicate system electrolyte to improve the corrosion resistance of the plasma electrolytic oxidation coating on Mg-9Li-3Al(wt%,LA93)alloy.The influences of carbonate on the morphology,struct...Carbonate was added to the silicate system electrolyte to improve the corrosion resistance of the plasma electrolytic oxidation coating on Mg-9Li-3Al(wt%,LA93)alloy.The influences of carbonate on the morphology,structure,and phase composition of the coating were investigated by scanning electron microscopy,energy dispersive spectrometry,X-ray diffraction,and X-ray photoelectron spectroscopy.The corrosion resistance of the coating was evaluated by electrochemical experiment,hydrogen evolution,and immersion test.The results showed that the addition of carbonate resulted in a denser coating with increased hardness,and the corrosion-resistant Li_(2)CO_(3) phase was formed.Electrochemical experiments showed that compared with the coating without carbonate,the corrosion potential of the carbonate coating positively shifted(24 mV),and the corrosion current density was reduced by approximately an order of magnitude.The coating with carbonate addition possessed a high corrosion resistance and long-term protection capability.展开更多
基金the Natural Science Foundation of China (Nos.51771060,51871068,51971071,and 52011530025)the Domain Foundation of Equipment Advance Research of 13th Five-year Plan,China(No.61409220118)+1 种基金the Zhejiang Province Key Research and Development Program,China (No.2021C01086)the Open Foundation of Key Laboratory of Superlight Materials&Surface Technology of Ministry of Education,China (No.HEU10202104)
文摘Carbonate was added to the silicate system electrolyte to improve the corrosion resistance of the plasma electrolytic oxidation coating on Mg-9Li-3Al(wt%,LA93)alloy.The influences of carbonate on the morphology,structure,and phase composition of the coating were investigated by scanning electron microscopy,energy dispersive spectrometry,X-ray diffraction,and X-ray photoelectron spectroscopy.The corrosion resistance of the coating was evaluated by electrochemical experiment,hydrogen evolution,and immersion test.The results showed that the addition of carbonate resulted in a denser coating with increased hardness,and the corrosion-resistant Li_(2)CO_(3) phase was formed.Electrochemical experiments showed that compared with the coating without carbonate,the corrosion potential of the carbonate coating positively shifted(24 mV),and the corrosion current density was reduced by approximately an order of magnitude.The coating with carbonate addition possessed a high corrosion resistance and long-term protection capability.