Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates （5.32-250.0μm/s） at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spac...Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates （5.32-250.0μm/s） at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spacing were measured from transverse sections of the samples.The dependences of the eutectic spacing and undercooling on growth rate are determined as λ=9.21V-0.53 and ΔT=0.0245V0.53,respectively.The results obtained in this work were compared with the Jackson-Hunt eutectic theory and the similar experimental results in the literature.Microhardness of directionally solidified samples was also measured by using a microhardness test device.The dependency of the microhardness on growth rate is found as Hv=115.64V0.13.Afterwards,the electrical resistivity （r） of the casting alloy changes from 40×10-9 to 108×10-9 Ω·m with the temperature rising in the range of 300-630 K.The enthalpy of fusion （ΔH） and specific heat （Cp） for the Zn-Al eutectic alloy are calculated to be 113.37 J/g and 0.309 J/（g·K）,respectively by means of differential scanning calorimetry （DSC） from heating trace during the transformation from liquid to solid.展开更多
基金supported by Erciyes University Scientific Research Project Unit (No.FBA-10-3376)
文摘Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates （5.32-250.0μm/s） at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spacing were measured from transverse sections of the samples.The dependences of the eutectic spacing and undercooling on growth rate are determined as λ=9.21V-0.53 and ΔT=0.0245V0.53,respectively.The results obtained in this work were compared with the Jackson-Hunt eutectic theory and the similar experimental results in the literature.Microhardness of directionally solidified samples was also measured by using a microhardness test device.The dependency of the microhardness on growth rate is found as Hv=115.64V0.13.Afterwards,the electrical resistivity （r） of the casting alloy changes from 40×10-9 to 108×10-9 Ω·m with the temperature rising in the range of 300-630 K.The enthalpy of fusion （ΔH） and specific heat （Cp） for the Zn-Al eutectic alloy are calculated to be 113.37 J/g and 0.309 J/（g·K）,respectively by means of differential scanning calorimetry （DSC） from heating trace during the transformation from liquid to solid.