Cryogenic insulation material rigid polyurethane(PU)foams were developed using bio-based and recycled feedstock.Polyols obtained from tall oil fatty acids produced as a side stream of wood biomass pulping and recycled...Cryogenic insulation material rigid polyurethane(PU)foams were developed using bio-based and recycled feedstock.Polyols obtained from tall oil fatty acids produced as a side stream of wood biomass pulping and recycled polyethylene terephthalate were used to develop rigid PU foam formulations.The 4th generation physical blowing agents with low global warming potential and low ozone depletion potential were used to develop rigid PU foam cryogenic insulation with excellent mechanical and thermal properties.Obtained rigid PU foams had a thermal conductivity coefficient as low as 0.0171 W/m·K and an apparent density of 37-40 kg/m^(3).The developed rigid PU foams had anisotropic compression strength properties,which were higher parallel to the foaming direction.Moreover,the compression strength was also influenced by the type of applied bio-based polyol.The bio-based polyols with higher OH group functionality delivered higher crosslinking density of polymer matrix;thus,the mechanical properties were also higher.The mechanical strength of the foams increased when materials were tested at liquid nitrogen temperature due to the stiffening of the polymer matrix.The thermal properties of the developed materials were determined using differential scanning calorimetry,dynamic mechanical analysis,and thermogravimetric analysis methods.Lastly,the developed rigid PU foams had good adhesion to the aluminium substrate before and after applying cyroshock and an excellent safety coefficient of 4-5.Rigid PU foams developed using Solstice LBA delivered adhesion strength of~0.5 MPa and may be considered for application as cryogenic insulation in the aerospace industry.展开更多
Early investigations of dielectric permittivity of rigid polyurethane foams at low frequencies were made on petrochemical-origin foams,mainly by means of parallel plate capacitors.In the present investigation biopolyo...Early investigations of dielectric permittivity of rigid polyurethane foams at low frequencies were made on petrochemical-origin foams,mainly by means of parallel plate capacitors.In the present investigation biopolyol was synthesized from Latvia-grown rapeseeds’oil by the transesterification method with triethanolamine,in an environmentally friendly process,without emission of harmful substances,at temperatures 175℃±5℃.Rigid,closed-cell rapeseed oil polyol polyurethane biofoams and petrochemical foams were made ensuring content of the renewable rapeseed oil polyol in ready foams 27 wt.%–29 wt.%.Dielectric permittivity of the polyurethane foams and the underlying monolithic petrochemical-origin polyurethane and biopolyurethane was measured with a non-destructive dielectric spectrometer equipped with a capacitive sensor of one-side access type at 16 discrete frequencies distributed geometrically over the band 10 Hz,…,330 kHz.Permittivity value of the gaseous phase in the closed-cells was estimated to beεg≈1.001 that corresponds to the values,characteristic for the most of gases.Dielectric permittivity of petrochemical polyurethane foams and the mentioned biofoams was compared with permittivity of polyurethane foams from industrial producers Sika JSC and General Plastics Manufacturing Co.Polyurethane foams of the developed formulation exhibit competitive,low dielectric permittivity,not exceeding that of the foams from industrial producers:petrochemical foams up to 550 kg/m^(3) and the mentioned biofoams,comprising the renewable rapeseed oil polyol,up to densities 230–250 kg/m^(3).Considering petrochemical-origin polyurethane foams as a heterogeneous media“Polymer—gaseous phase”,the applicability of the rule of mixture and Maxwell–Garnett equation to model mathematically the dependence of effective dielectric permittivity on the volume fraction of phases was showed.展开更多
In this work, free tall oil fatty acids were epoxidized with in-situ generated peroxyacetic acid. Reaction kineticsof epoxidation was investigated by oxirane content and iodine value titrimetric determination, as well...In this work, free tall oil fatty acids were epoxidized with in-situ generated peroxyacetic acid. Reaction kineticsof epoxidation was investigated by oxirane content and iodine value titrimetric determination, as well as FTIRspectra analysis. A highly functional biobased polyol was synthesized by functionalizing epoxidized tall oilfatty acids with triethanolamine using Montmorillonite K10 as a catalyst. The obtained polyol was analyzed byFTIR and MALDI-TOF MS. The most common chemical and physical characteristics of obtained polyol weredetermined.展开更多
基金funded by projects“Smart Materials,Photonics,Technologies and Engineering Ecosystem(MOTE)”(Contract No.VPP-EM-FOTONIKA-2022/1-0001)“Bio-Based Cryogenic Insulation for Aerospace Application(BioSpace)”(Contract No.4000135271/21/NL/SC).
文摘Cryogenic insulation material rigid polyurethane(PU)foams were developed using bio-based and recycled feedstock.Polyols obtained from tall oil fatty acids produced as a side stream of wood biomass pulping and recycled polyethylene terephthalate were used to develop rigid PU foam formulations.The 4th generation physical blowing agents with low global warming potential and low ozone depletion potential were used to develop rigid PU foam cryogenic insulation with excellent mechanical and thermal properties.Obtained rigid PU foams had a thermal conductivity coefficient as low as 0.0171 W/m·K and an apparent density of 37-40 kg/m^(3).The developed rigid PU foams had anisotropic compression strength properties,which were higher parallel to the foaming direction.Moreover,the compression strength was also influenced by the type of applied bio-based polyol.The bio-based polyols with higher OH group functionality delivered higher crosslinking density of polymer matrix;thus,the mechanical properties were also higher.The mechanical strength of the foams increased when materials were tested at liquid nitrogen temperature due to the stiffening of the polymer matrix.The thermal properties of the developed materials were determined using differential scanning calorimetry,dynamic mechanical analysis,and thermogravimetric analysis methods.Lastly,the developed rigid PU foams had good adhesion to the aluminium substrate before and after applying cyroshock and an excellent safety coefficient of 4-5.Rigid PU foams developed using Solstice LBA delivered adhesion strength of~0.5 MPa and may be considered for application as cryogenic insulation in the aerospace industry.
文摘Early investigations of dielectric permittivity of rigid polyurethane foams at low frequencies were made on petrochemical-origin foams,mainly by means of parallel plate capacitors.In the present investigation biopolyol was synthesized from Latvia-grown rapeseeds’oil by the transesterification method with triethanolamine,in an environmentally friendly process,without emission of harmful substances,at temperatures 175℃±5℃.Rigid,closed-cell rapeseed oil polyol polyurethane biofoams and petrochemical foams were made ensuring content of the renewable rapeseed oil polyol in ready foams 27 wt.%–29 wt.%.Dielectric permittivity of the polyurethane foams and the underlying monolithic petrochemical-origin polyurethane and biopolyurethane was measured with a non-destructive dielectric spectrometer equipped with a capacitive sensor of one-side access type at 16 discrete frequencies distributed geometrically over the band 10 Hz,…,330 kHz.Permittivity value of the gaseous phase in the closed-cells was estimated to beεg≈1.001 that corresponds to the values,characteristic for the most of gases.Dielectric permittivity of petrochemical polyurethane foams and the mentioned biofoams was compared with permittivity of polyurethane foams from industrial producers Sika JSC and General Plastics Manufacturing Co.Polyurethane foams of the developed formulation exhibit competitive,low dielectric permittivity,not exceeding that of the foams from industrial producers:petrochemical foams up to 550 kg/m^(3) and the mentioned biofoams,comprising the renewable rapeseed oil polyol,up to densities 230–250 kg/m^(3).Considering petrochemical-origin polyurethane foams as a heterogeneous media“Polymer—gaseous phase”,the applicability of the rule of mixture and Maxwell–Garnett equation to model mathematically the dependence of effective dielectric permittivity on the volume fraction of phases was showed.
文摘In this work, free tall oil fatty acids were epoxidized with in-situ generated peroxyacetic acid. Reaction kineticsof epoxidation was investigated by oxirane content and iodine value titrimetric determination, as well as FTIRspectra analysis. A highly functional biobased polyol was synthesized by functionalizing epoxidized tall oilfatty acids with triethanolamine using Montmorillonite K10 as a catalyst. The obtained polyol was analyzed byFTIR and MALDI-TOF MS. The most common chemical and physical characteristics of obtained polyol weredetermined.