Grain boundary and microstructure engineering of Inconel 690 cladding on stainless-steel 316L using electron-beam powder bed fusion additive manufacturing

This research explores the prospect of fabricating a face-centered cubic(fcc) Ni-base alloy cladding(Inconel 690) on an fcc Fe-base alloy(316 L stainless-steel) having improved mechanical properties and reduced sensitivity to corrosion through grain boundary and microstructure engineering concepts enabled by additive manufacturing(AM) utilizing electron-beam powder bed fusion(EPBF). The unique solidification and associated constitutional supercooling phenomena characteristic of EPBF promotes[100] textured and extended columnar grains having lower energy grain boundaries as opposed to random, high-angle grain boundaries, but no coherent {111} twin boundaries characteristic of conventional thermo-mechanically processed fcc metals and alloys, including Inconel 690 and 316 L stainless-steel.In addition to [100] textured grains, columnar grains were produced by EPBF fabrication of Inconel 690 claddings on 316 L stainless-steel substrates. Also, irregular 2–3 μm diameter, low energy subgrains were formed along with dislocation densities varying from 108 to 109 cm^2, and a homogeneous distribution of Cr_(23)C_6 precipitates. Precipitates were formed within the grains(with ~3 μm interparticle spacing),but not in the subgrain or columnar grain boundaries. These inclusive, hierarchical microstructures produced a tensile yield strength of 0.527 GPa, elongation of 21%, and Vickers microindentation hardness of 2.33 GPa for the Inconel 690 cladding in contrast to a tensile yield strength of 0.327 GPa, elongation of 53%, and Vickers microindentation hardness of 1.78 GPa, respectively for the wrought 316 L stainlesssteel substrate. Aging of both the Inconel 690 cladding and the 316 L stainless-steel substrate at 685?C for50 h precipitated Cr_(23)C_6 carbides in the Inconel 690 columnar grain boundaries, but not in the low-angle(and low energy) subgrain boundaries. In contrast, Cr_(23)C_6 carbides precipitated in the 316 L stainless-steel grain boundaries, but not in the low energy coherent {111} twin boundaries. Consequently, the Inconel690 subgrain boundaries essentially serve as surrogates for coherent twin boundaries with regard to avoiding carbide precipitation and corrosion sensitization.