The present paper reports Thermoluminescence (TL) Glow curve of Mn2+ doped CaAl2O4 phosphor with different UV exposure time. The Glow peak shows general order kinetics and evaluation of kinetic parameters was done by ...The present paper reports Thermoluminescence (TL) Glow curve of Mn2+ doped CaAl2O4 phosphor with different UV exposure time. The Glow peak shows general order kinetics and evaluation of kinetic parameters was done by peak shape method. Calculations of Trap Depth were done with Chen’s different methods and order of kinetics, activation energy and frequency factor are calculated. The recorded glow curve shifts towards higher temperature with increasing intensity as a function of UV exposure time until 30 minutes where it is seen that the peak shifts towards low temperature side and intensity also decreases. The peaks were found at 345?C, 356.83?C, 358?C and 356.73?C respectively using the heating rate 6.7?C/s. The PL (photoluminescence) excitation spectra show peaks at 248 nm and 362 nm whereas emission spectra shows peaks between 364 nm and 551 nm. Sample was characterized by XRD technique.展开更多
The properties of small amplitude acoustic waves (IAW) in unmagnetised plasma have been discussed in detail. An experimental set up to study the propagation of IAW in argon plasma has been descried. The speed of IAW u...The properties of small amplitude acoustic waves (IAW) in unmagnetised plasma have been discussed in detail. An experimental set up to study the propagation of IAW in argon plasma has been descried. The speed of IAW under different conditions of discharge current and pressure has been measured from the time-of flight technique. From these measurements, electron temperatures have been calculated. The results have been compared with those obtained by single probe method, and were found to be in good agreement with each other so IAW speeds can be used to calculate plasma parameters.展开更多
In this paper the effect of temperature on the mechanoluminescence of Au doped phosphors of（Zn,Cd）S is described.It is found that the ML disappears beyond a particular temperature.The temperature dependence of ML in...In this paper the effect of temperature on the mechanoluminescence of Au doped phosphors of（Zn,Cd）S is described.It is found that the ML disappears beyond a particular temperature.The temperature dependence of ML intensity follows the relation I =I_T^O（1-TIT_C）~n,where I_T^O is a constant,n is the slop of log I_T versus log（1- TIT_C） plot which lies between 0.9 and 1.10,T_C is the temperature at which ML disappear.It is found that the ML intensity in（Zn,Cd）S：Au disappear at 600 K.展开更多
文摘The present paper reports Thermoluminescence (TL) Glow curve of Mn2+ doped CaAl2O4 phosphor with different UV exposure time. The Glow peak shows general order kinetics and evaluation of kinetic parameters was done by peak shape method. Calculations of Trap Depth were done with Chen’s different methods and order of kinetics, activation energy and frequency factor are calculated. The recorded glow curve shifts towards higher temperature with increasing intensity as a function of UV exposure time until 30 minutes where it is seen that the peak shifts towards low temperature side and intensity also decreases. The peaks were found at 345?C, 356.83?C, 358?C and 356.73?C respectively using the heating rate 6.7?C/s. The PL (photoluminescence) excitation spectra show peaks at 248 nm and 362 nm whereas emission spectra shows peaks between 364 nm and 551 nm. Sample was characterized by XRD technique.
文摘The properties of small amplitude acoustic waves (IAW) in unmagnetised plasma have been discussed in detail. An experimental set up to study the propagation of IAW in argon plasma has been descried. The speed of IAW under different conditions of discharge current and pressure has been measured from the time-of flight technique. From these measurements, electron temperatures have been calculated. The results have been compared with those obtained by single probe method, and were found to be in good agreement with each other so IAW speeds can be used to calculate plasma parameters.
文摘In this paper the effect of temperature on the mechanoluminescence of Au doped phosphors of（Zn,Cd）S is described.It is found that the ML disappears beyond a particular temperature.The temperature dependence of ML intensity follows the relation I =I_T^O（1-TIT_C）~n,where I_T^O is a constant,n is the slop of log I_T versus log（1- TIT_C） plot which lies between 0.9 and 1.10,T_C is the temperature at which ML disappear.It is found that the ML intensity in（Zn,Cd）S：Au disappear at 600 K.