Nanocomposite multilayer TiBN coatings were prepared on Si(100) and 9Cr18Mo substrates using TiBN composite cathode plasma immersion ion implantation and deposition technique(PIIID). Synthesis of TiBN composite cathod...Nanocomposite multilayer TiBN coatings were prepared on Si(100) and 9Cr18Mo substrates using TiBN composite cathode plasma immersion ion implantation and deposition technique(PIIID). Synthesis of TiBN composite cathodes was conducted by powder metallurgy technology and the content of hexagonal boron nitride(h-BN) was changed from 8% to 40%(mass fraction). The as-deposited coatings were characterized by energy dispersive spectrometer(EDS), grazing incidence X-ray diffraction(GIXRD), Fourier Transform Infrared Spectroscopy(FTIR) and high resolution transmission electron microcopy(HRTEM). EDS results show that the B content of the coatings was varied from 3.71% to 13.84%(molar fraction) when the composition of the h-BN in the composited cathodes was changed from 8 % to 40%(mass fraction). GIXRD results reveal that the TiBN coatings with a B content of 8% has the main diffraction peak of TiN(200),(220) and(311), and these peaks disappear when the B content is increased. FTIR analysis of the multilayer coatings showed the presence of h-BN in all coatings. TEM images reveal that all coatings have the characteristics of self-forming nanocomposite multilayers, where the nanocomposites are composed of face-centered cubic Ti N or h-BN nanocrystalline embedded in amorphous matrix. The tribological tests reveal that the Ti BN coatings exhibit a marked decrease of coefficient at room temperature(~0.25). The improved properties were found to be derived from the comprehensiveness of the self-forming multilayers structure and the h-BN solid lubrication effects in the coatings.展开更多
Diamond-like carbon (DLC) films were synthesized by plasma immersion ion implantation and deposition (PIIID) on 9Cr18 bearing steel surface. Influences of working gas pressure and pulse width of the bias voltage on pr...Diamond-like carbon (DLC) films were synthesized by plasma immersion ion implantation and deposition (PIIID) on 9Cr18 bearing steel surface. Influences of working gas pressure and pulse width of the bias voltage on properties of the thin film were investigated. The chemical compositions of the as-deposited films were characterized by Raman spectroscopy. The micro-hardness, friction and wear behavior, corrosion resistance of the samples were evaluated, respectively. Compared with uncoated substrates, micro-hardness results reveal that the maximum is increased by 88.7%. In addition, the friction coefficient decreases to about 0.1, and the corrosion resistance of treated coupons surface are improved significantly.展开更多
基金Projects(21573054,21327002,51401201)supported by the National Natural Science Foundation of ChinaProject(U1537214)supported by the Joint Funds Key Project of the National Natural Science Foundation of ChinaProject(51535003)supported by the State Key Program of National Natural Science of China
文摘Nanocomposite multilayer TiBN coatings were prepared on Si(100) and 9Cr18Mo substrates using TiBN composite cathode plasma immersion ion implantation and deposition technique(PIIID). Synthesis of TiBN composite cathodes was conducted by powder metallurgy technology and the content of hexagonal boron nitride(h-BN) was changed from 8% to 40%(mass fraction). The as-deposited coatings were characterized by energy dispersive spectrometer(EDS), grazing incidence X-ray diffraction(GIXRD), Fourier Transform Infrared Spectroscopy(FTIR) and high resolution transmission electron microcopy(HRTEM). EDS results show that the B content of the coatings was varied from 3.71% to 13.84%(molar fraction) when the composition of the h-BN in the composited cathodes was changed from 8 % to 40%(mass fraction). GIXRD results reveal that the TiBN coatings with a B content of 8% has the main diffraction peak of TiN(200),(220) and(311), and these peaks disappear when the B content is increased. FTIR analysis of the multilayer coatings showed the presence of h-BN in all coatings. TEM images reveal that all coatings have the characteristics of self-forming nanocomposite multilayers, where the nanocomposites are composed of face-centered cubic Ti N or h-BN nanocrystalline embedded in amorphous matrix. The tribological tests reveal that the Ti BN coatings exhibit a marked decrease of coefficient at room temperature(~0.25). The improved properties were found to be derived from the comprehensiveness of the self-forming multilayers structure and the h-BN solid lubrication effects in the coatings.
文摘Diamond-like carbon (DLC) films were synthesized by plasma immersion ion implantation and deposition (PIIID) on 9Cr18 bearing steel surface. Influences of working gas pressure and pulse width of the bias voltage on properties of the thin film were investigated. The chemical compositions of the as-deposited films were characterized by Raman spectroscopy. The micro-hardness, friction and wear behavior, corrosion resistance of the samples were evaluated, respectively. Compared with uncoated substrates, micro-hardness results reveal that the maximum is increased by 88.7%. In addition, the friction coefficient decreases to about 0.1, and the corrosion resistance of treated coupons surface are improved significantly.