The electroless Ni-W-P coatings on polyoxymethylene(POM) were prepared. The POM was pretreated by hot spraying Al powder on it. Before the electroless Ni-W-P deposition, the POM with Al coating was flash plated in alk...The electroless Ni-W-P coatings on polyoxymethylene(POM) were prepared. The POM was pretreated by hot spraying Al powder on it. Before the electroless Ni-W-P deposition, the POM with Al coating was flash plated in alkaline bath. The mechanism of Ni-W-P deposition was studied and the technology was optimized. The XRD analysis shows that the "as-deposited" Ni-W-P plating has mixed crystalline structure. The hardness value of deposits is more than HV700. The abrasion resistance of deposits is six times more than that of POM. Bending test was used to determine the cohesion between the deposits and the substrates. SEM was used to study the behavior of surface abrasion and interface bonding condition. The reason for the excellent cohesion was interpreted.展开更多
文摘The electroless Ni-W-P coatings on polyoxymethylene(POM) were prepared. The POM was pretreated by hot spraying Al powder on it. Before the electroless Ni-W-P deposition, the POM with Al coating was flash plated in alkaline bath. The mechanism of Ni-W-P deposition was studied and the technology was optimized. The XRD analysis shows that the "as-deposited" Ni-W-P plating has mixed crystalline structure. The hardness value of deposits is more than HV700. The abrasion resistance of deposits is six times more than that of POM. Bending test was used to determine the cohesion between the deposits and the substrates. SEM was used to study the behavior of surface abrasion and interface bonding condition. The reason for the excellent cohesion was interpreted.