The oxidation tests of different SiC refractories including Si3N4-SiC bricks,Si3N4-Si2N2O-SiC bricks from China(SNO-1),Si3N4-Si2N2O-SiC bricks from overseas(SNO-2),SiAlON-SiC bricks,oxides bonded SiC bricks,self-bonde...The oxidation tests of different SiC refractories including Si3N4-SiC bricks,Si3N4-Si2N2O-SiC bricks from China(SNO-1),Si3N4-Si2N2O-SiC bricks from overseas(SNO-2),SiAlON-SiC bricks,oxides bonded SiC bricks,self-bonded SiC bricks as well as SiC castables were carried out in the steam atmosphere(1 000 ℃,32 kg·m-3·h-1)for different durations(100,200,300,400 and 500 h).The mass,the volume,the bulk density and the apparent porosity before and after the oxidation were tested.The XRD and SEM analyses were conducted.The results indicate that:(1)under the steam atmosphere condition(1 000 ℃,32 kg·m-3·h-1),as the oxidation time increases from 0 to 500 h,the volume and the mass of the silicon carbide refractories increase,while the bulk density decreases;in terms of the apparent porosity,oxides bonded SiC bricks and SiC castables present an increasing trend,Si3N4-SiC bricks,SiAlON-SiC bricks and self-bonded SiC bricks present an increasing trend first and then a decreasing trend,and Si3N4-Si2N2O-SiC bricks present a decreasing trend or a trend of decreasing first and then increasing;(2)as for Si3N4-Si2N2O-SiC bricks,SNO-1 and SNO-2 have basically the same chemical and phase composition,SNO-2 has the lower mass change rate than SNO-1 during oxidation from 200-500 h,which indicates that SNO-2 has the better steam oxidation resistance than SNO-1.展开更多
基金supported by Provincial Science&Technology Program(No.201200211500),Henan,China.
文摘The oxidation tests of different SiC refractories including Si3N4-SiC bricks,Si3N4-Si2N2O-SiC bricks from China(SNO-1),Si3N4-Si2N2O-SiC bricks from overseas(SNO-2),SiAlON-SiC bricks,oxides bonded SiC bricks,self-bonded SiC bricks as well as SiC castables were carried out in the steam atmosphere(1 000 ℃,32 kg·m-3·h-1)for different durations(100,200,300,400 and 500 h).The mass,the volume,the bulk density and the apparent porosity before and after the oxidation were tested.The XRD and SEM analyses were conducted.The results indicate that:(1)under the steam atmosphere condition(1 000 ℃,32 kg·m-3·h-1),as the oxidation time increases from 0 to 500 h,the volume and the mass of the silicon carbide refractories increase,while the bulk density decreases;in terms of the apparent porosity,oxides bonded SiC bricks and SiC castables present an increasing trend,Si3N4-SiC bricks,SiAlON-SiC bricks and self-bonded SiC bricks present an increasing trend first and then a decreasing trend,and Si3N4-Si2N2O-SiC bricks present a decreasing trend or a trend of decreasing first and then increasing;(2)as for Si3N4-Si2N2O-SiC bricks,SNO-1 and SNO-2 have basically the same chemical and phase composition,SNO-2 has the lower mass change rate than SNO-1 during oxidation from 200-500 h,which indicates that SNO-2 has the better steam oxidation resistance than SNO-1.