Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal t...Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal treatment at 200℃for 16 h show the best electrochemical properties,which deliver the high initial discharge capacity of 110.7 mA·h/g at 50 mA/g in potential window 2.0-4.0 V.To further improve their electrochemical properties,a ball milling process with graphene has been carried out to obtain Na0.44MnO2/graphene composite.The initial discharge capacity of Na0.44MnO2/graphene composite is 106.9 mA·h/g at a current density of 50 mA/g.After 100 cycles,the residual discharge capacity is 91.8 mA·h/g and the capacity retention rate is 85.9%,which is much higher than that of pristine Na0.44MnO2 nanorods(74.7%)at the same condition.What is more,when the current density reaches 500 and 1000 mA/g,the corresponding discharge capacities of Na0.44MnO2/graphene composite are about 89 and 78 mA·h/g,respectively,indicating outstanding rate capability.展开更多
Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indica...Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.展开更多
基金Project(51672234)supported by the National Natural Science Foundation of ChinaProject(1337304)supported by the Program for Innovative Research Cultivation Team in University,Ministry of Education,China
文摘Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal treatment at 200℃for 16 h show the best electrochemical properties,which deliver the high initial discharge capacity of 110.7 mA·h/g at 50 mA/g in potential window 2.0-4.0 V.To further improve their electrochemical properties,a ball milling process with graphene has been carried out to obtain Na0.44MnO2/graphene composite.The initial discharge capacity of Na0.44MnO2/graphene composite is 106.9 mA·h/g at a current density of 50 mA/g.After 100 cycles,the residual discharge capacity is 91.8 mA·h/g and the capacity retention rate is 85.9%,which is much higher than that of pristine Na0.44MnO2 nanorods(74.7%)at the same condition.What is more,when the current density reaches 500 and 1000 mA/g,the corresponding discharge capacities of Na0.44MnO2/graphene composite are about 89 and 78 mA·h/g,respectively,indicating outstanding rate capability.
基金Projects(51472211,51502256)supported by the National Natural Science Foundation of ChinaProjects(2016GK4005,2016GK4030)supported by the Strategic New Industry of Hunan Province,ChinaProject(13C925)supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.