Aiming at overcoming the difficulties in integral forming of thin-walled tubes with complex shapes, a novel forming method by inner and outer pressure through viscous was proposed. In this method, by dividing large de...Aiming at overcoming the difficulties in integral forming of thin-walled tubes with complex shapes, a novel forming method by inner and outer pressure through viscous was proposed. In this method, by dividing large deformation of the part into inner and outer pressure forming deformations, the limit deformation of tube part can be increased by several times. Meanwhile, the principle of viscous inner and outer pressure forming was provided, and key problems during the forming process such as reduction of the wall-thickness and instability wrinkling were analyzed. Thereby, the complex curved surface super-alloy GH3044 thin-walled tube with varying diameter ratio of 1.35（the ratio between the maximum and minimum diameters of the part） can be integrally formed by this method. The experimental surface of the formed part is superior in quality and the wall-thickness distribution is uniform. The results show that the viscous inner and outer pressure forming can provide a new approach for integral forming of thin-walled tubes with complex shapes.展开更多
Aiming at overcoming the low plasticity of magnesium alloy at room temperature, we researched viscous warm pressure bulging（VWPB） of AZ31B magnesium alloy based on the excellent thermal stability of viscous medium u...Aiming at overcoming the low plasticity of magnesium alloy at room temperature, we researched viscous warm pressure bulging（VWPB） of AZ31B magnesium alloy based on the excellent thermal stability of viscous medium under the warm forming condition. The potential improvements of plastic deformation ability and forming quality of AZ31B magnesium alloy are expected with the aid of thermal characteristics of viscous medium. During bulging process the velocity field variation and pressure stress field distribution of viscous medium are observed at different temperatures through which the effect of temperature on the mechanical property of viscous medium and AZ31B magnesium alloy are analyzed. The results show that the formability of AZ31B magnesium alloy increases first and then decreases as the temperature increases and it is the best at 200 ℃. On the other hand, the viscous medium which can build non-uniform pressure stress field also exhibits a good flow property at elevated temperature, and it is helpful to improving the formability of AZ31B magnesium alloy.展开更多
基金Funded by the National Natural Science Foundation of China(No.51205260)
文摘Aiming at overcoming the difficulties in integral forming of thin-walled tubes with complex shapes, a novel forming method by inner and outer pressure through viscous was proposed. In this method, by dividing large deformation of the part into inner and outer pressure forming deformations, the limit deformation of tube part can be increased by several times. Meanwhile, the principle of viscous inner and outer pressure forming was provided, and key problems during the forming process such as reduction of the wall-thickness and instability wrinkling were analyzed. Thereby, the complex curved surface super-alloy GH3044 thin-walled tube with varying diameter ratio of 1.35（the ratio between the maximum and minimum diameters of the part） can be integrally formed by this method. The experimental surface of the formed part is superior in quality and the wall-thickness distribution is uniform. The results show that the viscous inner and outer pressure forming can provide a new approach for integral forming of thin-walled tubes with complex shapes.
基金Funded by the National Natural Science Foundation of China(No.51575364)the Natural Science Foundation of Liaoning Province(No.2013024014)
文摘Aiming at overcoming the low plasticity of magnesium alloy at room temperature, we researched viscous warm pressure bulging（VWPB） of AZ31B magnesium alloy based on the excellent thermal stability of viscous medium under the warm forming condition. The potential improvements of plastic deformation ability and forming quality of AZ31B magnesium alloy are expected with the aid of thermal characteristics of viscous medium. During bulging process the velocity field variation and pressure stress field distribution of viscous medium are observed at different temperatures through which the effect of temperature on the mechanical property of viscous medium and AZ31B magnesium alloy are analyzed. The results show that the formability of AZ31B magnesium alloy increases first and then decreases as the temperature increases and it is the best at 200 ℃. On the other hand, the viscous medium which can build non-uniform pressure stress field also exhibits a good flow property at elevated temperature, and it is helpful to improving the formability of AZ31B magnesium alloy.