In this study,a roasting enhanced flotation process was proposed to recover LiMn_(2)O_(4) and grapite from waste lithium-ion batteries(LIBs).The effects of roasting temperature and time on the surface modification was...In this study,a roasting enhanced flotation process was proposed to recover LiMn_(2)O_(4) and grapite from waste lithium-ion batteries(LIBs).The effects of roasting temperature and time on the surface modification was investigated,and a series of analytical technologies were used to reveal process mechanism.The results indicate that LiMn_(2)O_(4) can be effectively separated from graphite via flotation after the roasting.The flotation grade of LiMn_(2)O_(4) was significantly increased from 63.10%to 91.36%after roasting at 550℃for 2 h.The TG-DTG analysis demonstrates that the difficulty in flotation separation of LiMn_(2)O_(4) from graphite is caused by the organic binder and electrolytes coating on their surfaces.The XRD,SEM,XPS,and contact angle analyses confirm that the organic films on the surfaces of those materials can be effectively removed by roasting,after which the wettability of LiMn_(2)O_(4) is regained and thus the surface wettability difference between the cathode and anode materials is increased significantly.The closed-circuit flotation test indicates that a LiMn_(2)O_(4) sample with high grade of 99.81%is obtained,while the recovery of LiMn_(2)O_(4) is as high as 99.40%.This study provides an economical and eco-friendly way to recycling waste LIBs.展开更多
基金Project(2021JJ20062) supported by the Natural Science Foundation of Hunan Province,ChinaProject(2019XK2304) supported by Landmark Innovation Demonstration Project of Hunan Province,China+3 种基金Project(2022GK4058) supported by High-tech Industry Science and Technology Innovation Leading Project of Hunan Province,ChinaProject(2020CX038) supported by the Innovation Driven Project of Central South University,ChinaProject(2019YFC1907301) supported by the National Key R&D Program of ChinaProject(202006375018) supported by the China Scholarship Council。
文摘In this study,a roasting enhanced flotation process was proposed to recover LiMn_(2)O_(4) and grapite from waste lithium-ion batteries(LIBs).The effects of roasting temperature and time on the surface modification was investigated,and a series of analytical technologies were used to reveal process mechanism.The results indicate that LiMn_(2)O_(4) can be effectively separated from graphite via flotation after the roasting.The flotation grade of LiMn_(2)O_(4) was significantly increased from 63.10%to 91.36%after roasting at 550℃for 2 h.The TG-DTG analysis demonstrates that the difficulty in flotation separation of LiMn_(2)O_(4) from graphite is caused by the organic binder and electrolytes coating on their surfaces.The XRD,SEM,XPS,and contact angle analyses confirm that the organic films on the surfaces of those materials can be effectively removed by roasting,after which the wettability of LiMn_(2)O_(4) is regained and thus the surface wettability difference between the cathode and anode materials is increased significantly.The closed-circuit flotation test indicates that a LiMn_(2)O_(4) sample with high grade of 99.81%is obtained,while the recovery of LiMn_(2)O_(4) is as high as 99.40%.This study provides an economical and eco-friendly way to recycling waste LIBs.
