Inorganic/organic poly（methylmethacrylate-acrylic acid-divinylbenzene） iron oxide Janus magnetic nanoparticles（P（MMA-AA-DVB）/Fe3O4） with strong magnetic domains and unique surface functionalities were prepared u...Inorganic/organic poly（methylmethacrylate-acrylic acid-divinylbenzene） iron oxide Janus magnetic nanoparticles（P（MMA-AA-DVB）/Fe3O4） with strong magnetic domains and unique surface functionalities were prepared using a solvothermal process.The P（MMA-AA-DVB） nanoparticles were prepared via soapfree emulsion polymerization and used as a precursor for preparing Janus nanoparticles.The morphology and magnetic properties of the magnetic Janus nanoparticles formed were characterized using a laser particle size analyzer,transmission electron microscopy,Fourier transform infrared spectroscopy,vibrating sample magnetometry,and thermogravimetric analysis.The synthesized P（MMA-AA-DVB）/Fe3O4 magnetic Janus nanoparticles were characterized by a Janus structure and possessed a stable asymmetric morphology after being dually functionalized.The particle size,magnetic content,and magnetic domain of the P（MMA-AA-DVB）/Fe3O4 magnetic Janus nanoparticles were 200 nm,40%,and 25 emu/g,respectively.The formation mechanism of the Janus nanoparticles was also investigated,and the results revealed that the reduction of Fe3＋ ions and growth of Fe3O4 took place on the surface of the P（MMA-AA-DVB） polymeric precursor particles.The size of the Janus particles could be controlled by narrowing the size distribution of the P（MMA-AA-DVB） precursor nanoparticles.展开更多
基金Project(51221001)supported by the National Natural Science Foundation of ChinaProject(B08040)supported by the Introducing Talents of Discipline to Universities,China
文摘Inorganic/organic poly（methylmethacrylate-acrylic acid-divinylbenzene） iron oxide Janus magnetic nanoparticles（P（MMA-AA-DVB）/Fe3O4） with strong magnetic domains and unique surface functionalities were prepared using a solvothermal process.The P（MMA-AA-DVB） nanoparticles were prepared via soapfree emulsion polymerization and used as a precursor for preparing Janus nanoparticles.The morphology and magnetic properties of the magnetic Janus nanoparticles formed were characterized using a laser particle size analyzer,transmission electron microscopy,Fourier transform infrared spectroscopy,vibrating sample magnetometry,and thermogravimetric analysis.The synthesized P（MMA-AA-DVB）/Fe3O4 magnetic Janus nanoparticles were characterized by a Janus structure and possessed a stable asymmetric morphology after being dually functionalized.The particle size,magnetic content,and magnetic domain of the P（MMA-AA-DVB）/Fe3O4 magnetic Janus nanoparticles were 200 nm,40%,and 25 emu/g,respectively.The formation mechanism of the Janus nanoparticles was also investigated,and the results revealed that the reduction of Fe3＋ ions and growth of Fe3O4 took place on the surface of the P（MMA-AA-DVB） polymeric precursor particles.The size of the Janus particles could be controlled by narrowing the size distribution of the P（MMA-AA-DVB） precursor nanoparticles.