To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the...To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures(200, 250, 300 and 350 ℃), while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum(with a range average of 235 MPa) and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51171059)the Innovative Research Team(in Science and Technology)in University of Henan Province(No.2012IRTSTHN008)the Basic and Frontier Technologies Research Plan of Henan Province(No.102300410018)
文摘To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures(200, 250, 300 and 350 ℃), while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum(with a range average of 235 MPa) and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.