To prepare the three-dimensional braided carbon fiber reinforced mullite （3D C/mullite） composites, an Al2O3-SiO2 solwith a solid content of 20% （mass fraction） and an Al2O3/SiO2 mass ratio of 2：1 was selected as...To prepare the three-dimensional braided carbon fiber reinforced mullite （3D C/mullite） composites, an Al2O3-SiO2 solwith a solid content of 20% （mass fraction） and an Al2O3/SiO2 mass ratio of 2：1 was selected as the raw material. Characteristics andmullitization of the sol were analyzed throughly. It is found that the formation of mullite is basically completed at 1300℃ and thegel powders exhibit favorable sintering shrinkage. The 3D C/mullite composites without interfacial coating were fabricated throughthe route of vacuum impregnation-drying-heat treatment. Satisfied mechanical properties with a flexural strength of 241.2 MPa anda fracture toughness of 10.9 MPa·m1/2are obtained although the total porosity reaches 26.0%. Oxidation resistances of the compositesat 1200, 1400 and 1600 ℃ were investigated. Due to the further densification of matrix, the 3D C/mullite composites show tiny massloss and their mechanical properties are well retained after oxidation at 1600 ℃ for 30 min.展开更多
基金Project(SAST2015043)supported by the Science Innovation Foundation of Shanghai Academy of Spaceflight Technology,ChinaProject(614291102010117)supported by the Open Foundation of Science and Technology on Thermostructural Composite Materials Laboratory,ChinaProject(11572277)supported by the National Natural Science Foundation of China
文摘To prepare the three-dimensional braided carbon fiber reinforced mullite （3D C/mullite） composites, an Al2O3-SiO2 solwith a solid content of 20% （mass fraction） and an Al2O3/SiO2 mass ratio of 2：1 was selected as the raw material. Characteristics andmullitization of the sol were analyzed throughly. It is found that the formation of mullite is basically completed at 1300℃ and thegel powders exhibit favorable sintering shrinkage. The 3D C/mullite composites without interfacial coating were fabricated throughthe route of vacuum impregnation-drying-heat treatment. Satisfied mechanical properties with a flexural strength of 241.2 MPa anda fracture toughness of 10.9 MPa·m1/2are obtained although the total porosity reaches 26.0%. Oxidation resistances of the compositesat 1200, 1400 and 1600 ℃ were investigated. Due to the further densification of matrix, the 3D C/mullite composites show tiny massloss and their mechanical properties are well retained after oxidation at 1600 ℃ for 30 min.