Increasing porosity is one of the most direct ways to improve the thermal insulation and dielectric properties of materials.Until now,many wet methods for preparing Si_(3)N_(4) ceramic foams usually face the problems ...Increasing porosity is one of the most direct ways to improve the thermal insulation and dielectric properties of materials.Until now,many wet methods for preparing Si_(3)N_(4) ceramic foams usually face the problems of complex rheology,long period,and expensive cost,and the reported pore sizes of Si_(3)N_(4) ceramic foams are typically micron-grade,resulting in a lack of competitiveness in thermal insulation and wave-transparent applications.In this paper,the Si_(3)N_(4)@SiO_(2) ceramic foams were prepared using an efficient dry-method,which combined three processes of low temperature chemical vapor deposition(LTCVD),template,and isostatic pressing.The method has the advantages of simple operation and short preparation period,and can realize near-net size molding and mass production.In addition,the evolution mechanisms of honeycomb microstructure and composition of Si_(3)N_(4)@SiO_(2) ceramic foam during sintering were studied by chemical reaction thermodynamics.The as-prepared Si_(3)N_(4)@SiO_(2) ceramic foam possesses low density(0.377 g·cm^(-3)),high compressive strength(7.5 MPa),low thermal conductivity(0.0808 W·m^(-1)·K^(-1)),and excellent dielectric properties(ε<1.32,tanδ<0.009)in the frequency range of 8-18 GHz,and its maximum working temperature in air can reach up to 1100℃.It will be recommended to be applied in the interlayer of Si_(3)N_(4) ceramic radome to improve its thermal insulation and electromagnetic wave transparency performances.展开更多
基金supported by the Special Project of Science and Technology Cooperation and Exchange of Shanxi Province(No.202204041101014)the National Key Research and Development Program of China(No.2023YFB3811302)+1 种基金the Jinzhong University Research Funds for Doctor(No.JUD2023014)the Shanxi Provincial Key Research and Development Project(No.2022ZDYF027).
文摘Increasing porosity is one of the most direct ways to improve the thermal insulation and dielectric properties of materials.Until now,many wet methods for preparing Si_(3)N_(4) ceramic foams usually face the problems of complex rheology,long period,and expensive cost,and the reported pore sizes of Si_(3)N_(4) ceramic foams are typically micron-grade,resulting in a lack of competitiveness in thermal insulation and wave-transparent applications.In this paper,the Si_(3)N_(4)@SiO_(2) ceramic foams were prepared using an efficient dry-method,which combined three processes of low temperature chemical vapor deposition(LTCVD),template,and isostatic pressing.The method has the advantages of simple operation and short preparation period,and can realize near-net size molding and mass production.In addition,the evolution mechanisms of honeycomb microstructure and composition of Si_(3)N_(4)@SiO_(2) ceramic foam during sintering were studied by chemical reaction thermodynamics.The as-prepared Si_(3)N_(4)@SiO_(2) ceramic foam possesses low density(0.377 g·cm^(-3)),high compressive strength(7.5 MPa),low thermal conductivity(0.0808 W·m^(-1)·K^(-1)),and excellent dielectric properties(ε<1.32,tanδ<0.009)in the frequency range of 8-18 GHz,and its maximum working temperature in air can reach up to 1100℃.It will be recommended to be applied in the interlayer of Si_(3)N_(4) ceramic radome to improve its thermal insulation and electromagnetic wave transparency performances.
