The role of Nd solid-solution and grain-boundary segregation in binary NiAl alloy was studied based on microhardness and compressive macrostrain. X-ray and Auger spectra studies indicate that Nd not only is soluble in...The role of Nd solid-solution and grain-boundary segregation in binary NiAl alloy was studied based on microhardness and compressive macrostrain. X-ray and Auger spectra studies indicate that Nd not only is soluble in grain interiors, but also segregates to the grain boundaries. Nd solid-solution induces an increase of the microhardness from 269 to 290 HV in grain interiors and segregation results in an enhancement of hardness from 252 to 342 HV on grain boundaries. Thus, the cohesion of grain boundaries is enhanced by Nd segregation, which make the alloy doped with 0.05 wt pct Nd exhibit more compressive microstrain, i.e. the higher the compressive ductility at room temperature, the better the final surface condition at elevated temperature. Finally, a discussion was made on the reason that Nd strengthens the grain boundaries in NiAl intermetallic alloy.展开更多
The influence of strain rate and temperature on the tensile behavior of as-cast and HIPed NiAI-9Mo eutectic alloy was investigated in the temperature range of 700-950℃ and over a strain rate range from 2.08×10-4...The influence of strain rate and temperature on the tensile behavior of as-cast and HIPed NiAI-9Mo eutectic alloy was investigated in the temperature range of 700-950℃ and over a strain rate range from 2.08×10-4 s-1 to 2.08×10-2 s-1. The results indicate that HIP process causes an enhancement in ductility and a decrease in ultimate tensile strength (UTS), yield strength (YS), average strain hardening rate as well as a drop in brittle to ductile transition temperature(BDTT) under the same condition. It is noticed that the BDTT of as-cast NiAI-9Mo is more dependent on strain rate than that of HIPed one. The brittle to ductile transition process of the alloy is related to a sharp drop in strain hardening rate. Regardless of strain rate, the fracture morphology changes from cleavage in NiAl phase and debonding along NiAI/Mo interface below the BDTT to microvoid coalescence above BDTT. The apparent activation energy of the BDT of HIPed and as-cast material are calculated to be 327 and 263 kJ/mol, respectively, suggesting that the mechanism is associated with lattice diffusion in NiAl phase.展开更多
文摘The role of Nd solid-solution and grain-boundary segregation in binary NiAl alloy was studied based on microhardness and compressive macrostrain. X-ray and Auger spectra studies indicate that Nd not only is soluble in grain interiors, but also segregates to the grain boundaries. Nd solid-solution induces an increase of the microhardness from 269 to 290 HV in grain interiors and segregation results in an enhancement of hardness from 252 to 342 HV on grain boundaries. Thus, the cohesion of grain boundaries is enhanced by Nd segregation, which make the alloy doped with 0.05 wt pct Nd exhibit more compressive microstrain, i.e. the higher the compressive ductility at room temperature, the better the final surface condition at elevated temperature. Finally, a discussion was made on the reason that Nd strengthens the grain boundaries in NiAl intermetallic alloy.
基金The authors gratefully acknowledge the National Natural Science Foundation of China for its financial support under the contract No.59895152.
文摘The influence of strain rate and temperature on the tensile behavior of as-cast and HIPed NiAI-9Mo eutectic alloy was investigated in the temperature range of 700-950℃ and over a strain rate range from 2.08×10-4 s-1 to 2.08×10-2 s-1. The results indicate that HIP process causes an enhancement in ductility and a decrease in ultimate tensile strength (UTS), yield strength (YS), average strain hardening rate as well as a drop in brittle to ductile transition temperature(BDTT) under the same condition. It is noticed that the BDTT of as-cast NiAI-9Mo is more dependent on strain rate than that of HIPed one. The brittle to ductile transition process of the alloy is related to a sharp drop in strain hardening rate. Regardless of strain rate, the fracture morphology changes from cleavage in NiAl phase and debonding along NiAI/Mo interface below the BDTT to microvoid coalescence above BDTT. The apparent activation energy of the BDT of HIPed and as-cast material are calculated to be 327 and 263 kJ/mol, respectively, suggesting that the mechanism is associated with lattice diffusion in NiAl phase.