Oxide formation mechanism of a corrosion-resistant CZ1 zirconium alloy

Tailoring microstructure and microchemistry by altering elemental compositions and thermomechanical treatment parameters enables superior corrosion performance in zirconium alloys for nuclear applications.However,our understanding of the relationship between various defects and the corrosion process remains limited in the newly developed zirconium alloys.Here we report the oxide formation mechanism of a CZ1 zirconium alloy with corrosion resistance surpassing many other zirconium alloy systems,such as Zircaloy-4 and Zr-1Nb-1Sn alloys.Autoclave experiments of CZ1 alloy and Zr1Nb-1Sn model alloy were performed in 360°C water for up to 820 d.We quantitively determined oxide phases by transmission Kikuchi diffraction(TKD)and examined lateral cracks,nano-porosity,and second-phase particles in oxide scales by transmission electron microscopy(TEM).Compared to the Zr-1Nb-1Sn model alloy,CZ1 alloy with lower Nb and Sn concentrations has shown smaller and lower-density lateral cracks but slightly larger oxide grains,reducing the diffusion route for oxidating species.Using analytical scanning and transmission electron microscopy,we demonstrate that due to the lower content of Sn(∼0.9 wt.%),there is less tetragonal ZrO_(2) phase formed in the oxide,and the level of tetragonal to the monoclinic phase transition is reduced.Although the Nb content(0.1 wt.%–0.3 wt.%)is lower than the solid solution limit of Nb in Zr,by introducing minor elements such as Fe,Cr,and Cu,there are still a reasonable number of second-phase particles to relieve the high stress associated with the metal-to-oxide transformation.These mechanisms have substantially changed the density and distribution of lateral cracks in the oxide,thus reducing the corrosion rate of zirconium alloys.

Enhanced tensile ductility of tungsten microwires via high-density dislocations and reduced grain boundaries

Despite being strong with many outstanding physical properties,tungsten is inherently brittle at room temperature,restricting its structural and functional applications at small scales.Here,a facile strategy has been adopted,to introduce high-density dislocations while reducing grain boundaries,through electron backscatter diffraction(EBSD)-guided microfabrication of cold-drawn bulk tungsten wires.The designed tungsten microwire attains an ultralarge uniform tensile elongation of~10.6%,while retains a high yield strength of~2.4 GPa.in situ TEM tensile testing reveals that the large uniform elongation of tungsten microwires originates from the motion of pre-existing high-density dislocations,while the subsequent ductile fracture is attributed to crack-tip plasticity and the inhibition of grain boundary cracking.This work demonstrates the application potential of tungsten microcomponents with superior ductility and workability for micro/nanoscale mechanical,electronic,and energy systems.