To enhance the microbiologically influenced corrosion(MIC)resistance of FeCoNiCrMn high entropy alloy(HEAs),a series of Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs were prepared.Microstructural characteristics...To enhance the microbiologically influenced corrosion(MIC)resistance of FeCoNiCrMn high entropy alloy(HEAs),a series of Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs were prepared.Microstructural characteristics,corrosion behavior(morphology observation and electrochemical properties),and antimicrobial performance of Fe_(x)Cu_((1−x))CoNiCrMn HEAs were evaluated in a medium inoculated with typical corrosive microorganism Pseudomonas aeruginosa.The aim was to identify copper-containing FeCoNiCrMn HEAs that balance corrosion resistance and antimicrobial properties.Results revealed that all Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs exhibited an FCC(face centered cubic)phase,with significant grain refinement observed in Fe_(0.75)Cu_(0.25)CoNiCrMn HEA.Electrochemical tests indicated that Fe_(0.75)Cu_(0.25)CoNiCrMn HEA demonstrated lower corrosion current density(i_(corr))and pitting potential(E_(pit))compared to other Fe_(x)Cu_((1−x))CoNiCrMn HEAs in P.aeruginosa-inoculated medium,exhibiting superior resistance to MIC.Anti-microbial tests showed that after 14 d of immersion,Fe_(0.75)Cu_(0.25)CoNiCrMn achieved an antibacterial rate of 89.5%,effectively inhibiting the adhesion and biofilm formation of P.aeruginosa,thereby achieving resistance to MIC.展开更多
In this work,the microbiologically influenced corrosion(MIC)of Fe_(40)(CoCrMnNi)_(60) and Fe_(60)(CoCrMnNi)_(40) medium entropy alloys(MEAs)induced by Pseudomonas aeruginosa(P.aeruginosa)was investigated.Corrosion beh...In this work,the microbiologically influenced corrosion(MIC)of Fe_(40)(CoCrMnNi)_(60) and Fe_(60)(CoCrMnNi)_(40) medium entropy alloys(MEAs)induced by Pseudomonas aeruginosa(P.aeruginosa)was investigated.Corrosion behaviors during 14 days of immersion in sterile and P.aeruginosa-inoculated culture media are presented.Under sterile conditions,both MEAs exhibited good corrosion resistance against the culture medium solution.In the presence of P.aeruginosa,the pitting corrosion of MEAs was promoted.The results of inductively coupled plasma‒mass spectrometry(ICP‒MS)and potentiodynamic polarization tests showed that the presence of P.aeruginosa promoted the selective dissolution of passive film and accelerated the corrosion of MEAs.The results of X-ray photoelectron spectroscopy(XPS)and Mott-Schottky measurements further demonstrated the degradation effect of P.aeruginosa on the passive film.Compared with Fe_(60)(CoCrMnNi)_(40),Fe_(40)(CoCrMnNi)_(60) manifested better resistance to the MIC caused by P.aeruginosa,which may be attributed to more Cr oxides and fewer Fe oxides of the passive film.展开更多
基金supported by the China Postdoctoral Science Foundation(No.2022M720401)the Postdoctoral Research Foundation of Shunde Innovation School,University of Science and Technology Beijing(No.2022BH007)the National Natural Science Foundation of China(No.52301074).
文摘To enhance the microbiologically influenced corrosion(MIC)resistance of FeCoNiCrMn high entropy alloy(HEAs),a series of Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs were prepared.Microstructural characteristics,corrosion behavior(morphology observation and electrochemical properties),and antimicrobial performance of Fe_(x)Cu_((1−x))CoNiCrMn HEAs were evaluated in a medium inoculated with typical corrosive microorganism Pseudomonas aeruginosa.The aim was to identify copper-containing FeCoNiCrMn HEAs that balance corrosion resistance and antimicrobial properties.Results revealed that all Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs exhibited an FCC(face centered cubic)phase,with significant grain refinement observed in Fe_(0.75)Cu_(0.25)CoNiCrMn HEA.Electrochemical tests indicated that Fe_(0.75)Cu_(0.25)CoNiCrMn HEA demonstrated lower corrosion current density(i_(corr))and pitting potential(E_(pit))compared to other Fe_(x)Cu_((1−x))CoNiCrMn HEAs in P.aeruginosa-inoculated medium,exhibiting superior resistance to MIC.Anti-microbial tests showed that after 14 d of immersion,Fe_(0.75)Cu_(0.25)CoNiCrMn achieved an antibacterial rate of 89.5%,effectively inhibiting the adhesion and biofilm formation of P.aeruginosa,thereby achieving resistance to MIC.
基金financially supported by the National Natural Science Foundation of China(Nos.52001021,52161160308)the China Postdoctoral Science Foundation(Nos.2021M700372 and 2021M700381)+1 种基金the Joint Fund of Basic and Applied Basic Research Fund of Guangdong Province(No.2021B1515130009)the Open Fund from State Key Laboratory of Metal Material for Marine Equipment and Application(No.SKLMEA-K202006).
文摘In this work,the microbiologically influenced corrosion(MIC)of Fe_(40)(CoCrMnNi)_(60) and Fe_(60)(CoCrMnNi)_(40) medium entropy alloys(MEAs)induced by Pseudomonas aeruginosa(P.aeruginosa)was investigated.Corrosion behaviors during 14 days of immersion in sterile and P.aeruginosa-inoculated culture media are presented.Under sterile conditions,both MEAs exhibited good corrosion resistance against the culture medium solution.In the presence of P.aeruginosa,the pitting corrosion of MEAs was promoted.The results of inductively coupled plasma‒mass spectrometry(ICP‒MS)and potentiodynamic polarization tests showed that the presence of P.aeruginosa promoted the selective dissolution of passive film and accelerated the corrosion of MEAs.The results of X-ray photoelectron spectroscopy(XPS)and Mott-Schottky measurements further demonstrated the degradation effect of P.aeruginosa on the passive film.Compared with Fe_(60)(CoCrMnNi)_(40),Fe_(40)(CoCrMnNi)_(60) manifested better resistance to the MIC caused by P.aeruginosa,which may be attributed to more Cr oxides and fewer Fe oxides of the passive film.