To alleviate deck fatigue failure and regular pavement damage,which are congenital deficiencies of highway steel bridge deck structure,this paper proposes a newtype of composite bridge deck,consisting of steel tubular...To alleviate deck fatigue failure and regular pavement damage,which are congenital deficiencies of highway steel bridge deck structure,this paper proposes a newtype of composite bridge deck,consisting of steel tubular connectors and steel-reactive powder concrete (RPC). Push-out tests were conducted to study the newdeck's shear performance. During the experimental process,specimens were divided into two groups which are composed of steel tubular connectors with or without penetrative bars set in. Then,researchers analyzed destroyed models and mechanisms of the composite structure under shear forces. Results showed that test models in two groups,once destroyed,displayed similar shear fracture,which appeared on the lower margin of the steel tubular wall along the welds. Meanwhile,RPC under the connector,for varied tests,was crushed at the same stage,although the large shear and bending deformation just occurred on connectors with penetrative bars. Additionally,shear capacity of specimens with penetrative bars,compared with the ones without bars,unexpectedly decreased by 20%,but the structural ductility was 1.75 times as much,and the ductility coefficients of specimens were all larger than 3.5,demonstrating certain deformation capacity.展开更多
Steel and ultra⁃high performance concrete(UHPC)composite decks are effective at reducing fatigue cracking and asphalt pavement damage.The shear behavior of innovative open steel tube(OST)connectors in steel⁃UHPC compo...Steel and ultra⁃high performance concrete(UHPC)composite decks are effective at reducing fatigue cracking and asphalt pavement damage.The shear behavior of innovative open steel tube(OST)connectors in steel⁃UHPC composite decks was investigated by conducting push⁃out tests.The test parameter is the presence of reinforcement in the deck.The load⁃slip curves and shear behavior of the push⁃out specimens were obtained and discussed.The test results indicate that as compared with plain concrete specimens,the limit slip of reinforced specimens decreased by 32%and the shear stiffness increased by 10%,but the ultimate shear capacity was almost the same.The use of UHPC influenced the failure process as it was observed that the OST connector was sheared off at its lower semi⁃tube,followed by the pull⁃out failure of the upper semi⁃tube.A finite element model was verified by tests and was then used to analyze the deformation and failure behaviors of the composite deck with open tubes.The model demonstrates that there is a stress concentration zone at the connector root,and the lower semi⁃tube is the main component that is subject to loads.展开更多
基金Sponsored by the National Natural Science Foundation of China(Grant No.51478120)
文摘To alleviate deck fatigue failure and regular pavement damage,which are congenital deficiencies of highway steel bridge deck structure,this paper proposes a newtype of composite bridge deck,consisting of steel tubular connectors and steel-reactive powder concrete (RPC). Push-out tests were conducted to study the newdeck's shear performance. During the experimental process,specimens were divided into two groups which are composed of steel tubular connectors with or without penetrative bars set in. Then,researchers analyzed destroyed models and mechanisms of the composite structure under shear forces. Results showed that test models in two groups,once destroyed,displayed similar shear fracture,which appeared on the lower margin of the steel tubular wall along the welds. Meanwhile,RPC under the connector,for varied tests,was crushed at the same stage,although the large shear and bending deformation just occurred on connectors with penetrative bars. Additionally,shear capacity of specimens with penetrative bars,compared with the ones without bars,unexpectedly decreased by 20%,but the structural ductility was 1.75 times as much,and the ductility coefficients of specimens were all larger than 3.5,demonstrating certain deformation capacity.
基金Sponsored by the National Natural Science Foundation of China(Grant No.51478120)。
文摘Steel and ultra⁃high performance concrete(UHPC)composite decks are effective at reducing fatigue cracking and asphalt pavement damage.The shear behavior of innovative open steel tube(OST)connectors in steel⁃UHPC composite decks was investigated by conducting push⁃out tests.The test parameter is the presence of reinforcement in the deck.The load⁃slip curves and shear behavior of the push⁃out specimens were obtained and discussed.The test results indicate that as compared with plain concrete specimens,the limit slip of reinforced specimens decreased by 32%and the shear stiffness increased by 10%,but the ultimate shear capacity was almost the same.The use of UHPC influenced the failure process as it was observed that the OST connector was sheared off at its lower semi⁃tube,followed by the pull⁃out failure of the upper semi⁃tube.A finite element model was verified by tests and was then used to analyze the deformation and failure behaviors of the composite deck with open tubes.The model demonstrates that there is a stress concentration zone at the connector root,and the lower semi⁃tube is the main component that is subject to loads.