The multi-walled carbon nanotube was introduced into the polymer matrix (PANI) to improve the electric conductivity as well as mechanical properties of the original polymer matrix.PANI/multi-walled carbon nanotube (MW...The multi-walled carbon nanotube was introduced into the polymer matrix (PANI) to improve the electric conductivity as well as mechanical properties of the original polymer matrix.PANI/multi-walled carbon nanotube (MWCNT) composites were synthesized via ex-situ and in-situ polymerization to improve their electrical property.And the DC conductivities of PANI/MWCNT according to content and diameter of MWCNT were measured by four-point probe.The highest electric conductivity of PANI/MWCNT composite is 20 S/cm when 0.3% (mass fraction) MWCNTs with 10 nm in diameter and 15 μm in length are added in composite.展开更多
A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacryla...A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacrylate and styrene were synthesized by emulsion polymerization. And the effect of comonomer composition on the thermal property of polymer core particle was investigated. By electroless plating method, the nickel particles were formed and deposited on the surface of P(BA-co-Sty) particles to form P(BA-co-Sty) core-nickel shell composite particles. SEM observation confirms that the nickel particles with size of 15 nm are distributed on the surface of the polymer core particles. The surface resistance of P(BA-co-Sty) core-nickel shell composite is 0.8×108Ω/cm2, enough to act as antistatic coating material.展开更多
基金project(2012-0007594)supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Education,Science and Technology
文摘The multi-walled carbon nanotube was introduced into the polymer matrix (PANI) to improve the electric conductivity as well as mechanical properties of the original polymer matrix.PANI/multi-walled carbon nanotube (MWCNT) composites were synthesized via ex-situ and in-situ polymerization to improve their electrical property.And the DC conductivities of PANI/MWCNT according to content and diameter of MWCNT were measured by four-point probe.The highest electric conductivity of PANI/MWCNT composite is 20 S/cm when 0.3% (mass fraction) MWCNTs with 10 nm in diameter and 15 μm in length are added in composite.
基金supported by the Korea Research Foundation Grant funded by the Korean Government (MOEHRD,Basic Research Promotion Fund) (KRF-2007-313-D00212)
文摘A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacrylate and styrene were synthesized by emulsion polymerization. And the effect of comonomer composition on the thermal property of polymer core particle was investigated. By electroless plating method, the nickel particles were formed and deposited on the surface of P(BA-co-Sty) particles to form P(BA-co-Sty) core-nickel shell composite particles. SEM observation confirms that the nickel particles with size of 15 nm are distributed on the surface of the polymer core particles. The surface resistance of P(BA-co-Sty) core-nickel shell composite is 0.8×108Ω/cm2, enough to act as antistatic coating material.