A(ZrC/SiC)_(3)alternate coating was deposited on sharp leading edge(SLE)C/C composites by chemical vapor deposition(CVD).The ablation behavior was examined via oxyacetylene torch with heat flux of 2.38 MW/m^2.The resu...A(ZrC/SiC)_(3)alternate coating was deposited on sharp leading edge(SLE)C/C composites by chemical vapor deposition(CVD).The ablation behavior was examined via oxyacetylene torch with heat flux of 2.38 MW/m^2.The results indicated that the alternate coating exhibited great ablation resistance,providing an effective protection for C/C composites.In initial rapid heating stage,the(ZrC/SiC)_(3) alternate coating can relieve thermal stress,avoiding the peeling of coating and keeping an intact coating structure.In subsequent ablation,the Si C layers in central region were consumed rapidly,leaving layered interspaces.Three stacked ZrO_(2) layers were reserved with the assistance of the release of thermal stress by interspaces,offering a great anti-scouring effect.In transition and border regions,the alternate Si C layers can delay oxygen erosion of inner coating and C/C substrate by the formation of SiO_(2).It is believed that the results would be helpful for the design and application of anti-ablation coatings on SLE C/C composites.展开更多
基金the National Natural Science Foundation of China(Nos.51727804,51821091,51872233)Natural Science Basic Research Plan in Shaanxi Province of China(No.2020JQ-175)。
文摘A(ZrC/SiC)_(3)alternate coating was deposited on sharp leading edge(SLE)C/C composites by chemical vapor deposition(CVD).The ablation behavior was examined via oxyacetylene torch with heat flux of 2.38 MW/m^2.The results indicated that the alternate coating exhibited great ablation resistance,providing an effective protection for C/C composites.In initial rapid heating stage,the(ZrC/SiC)_(3) alternate coating can relieve thermal stress,avoiding the peeling of coating and keeping an intact coating structure.In subsequent ablation,the Si C layers in central region were consumed rapidly,leaving layered interspaces.Three stacked ZrO_(2) layers were reserved with the assistance of the release of thermal stress by interspaces,offering a great anti-scouring effect.In transition and border regions,the alternate Si C layers can delay oxygen erosion of inner coating and C/C substrate by the formation of SiO_(2).It is believed that the results would be helpful for the design and application of anti-ablation coatings on SLE C/C composites.