An upconversion luminescence powder TiO2:(Er3+,Yb3+) is prepared by a hydrothermal method and used to fabricate dye-sensitized solar cell (DSSC).The TiO2:(Er3+,Yb3+) powder undergoes upconversion luminescence,converti...An upconversion luminescence powder TiO2:(Er3+,Yb3+) is prepared by a hydrothermal method and used to fabricate dye-sensitized solar cell (DSSC).The TiO2:(Er3+,Yb3+) powder undergoes upconversion luminescence,converting infrared light which the dye can not absorb into visible light with wavelengths of 510-700 nm which the dye can absorb,increasing the photocurrent of the DSSC.TiO2:(Er3+,Yb3+) also acts as a p-type dopant,heightening the Fermi level of the oxide film,which increases the photovoltage of the DSSC.The best performance of the DSSC is found when the ratio of TiO2/luminescence powder is 1/3 in the luminescence layer.Under simulated solar irradiation of 100 mW cm-2 (AM 1.5),the DSSC containing TiO2:(Er3+,Yb3+) doping achieves a light-to-electricity energy conversion efficiency of 7.28% compared with 6.41% for the undoped DSSC.展开更多
Mesoporous TiO2microsphere(MTM)was synthesized via a simple solution route and then mixed with commercial TiO2(P25)to form highly homogeneous and stable TiO2colloid by simple hydrothermal treatment.The TiO2colloid was...Mesoporous TiO2microsphere(MTM)was synthesized via a simple solution route and then mixed with commercial TiO2(P25)to form highly homogeneous and stable TiO2colloid by simple hydrothermal treatment.The TiO2colloid was coated onto the plastic conductive substrate to prepare mesoporous TiO2film for flexible dye-sensitized solar cells(DSSCs)by low-temperature heat treatment.The influence of MTM content on the physicochemical properties of the flexible TiO2film was characterized by scanning electron microscope,transmission electron microscopy,X-ray diffraction,energy-dispersive X-ray spectrometer,N2adsorption-desorption isotherms,UV–vis absorption and diffuse reflectance spectra.It is revealed that with increasing the MTM content,the dye-loading capability of TiO2film and light-harvesting efficiency of flexible DSSCs are improved due to MTM having high surface area and acting as a light scattering center,respectively,resulting in the enhancement of photocurrent of flexible DSSCs.However,more and larger cracks having negative effect on the performances of flexible DSSCs are formed simultaneously.Under the optimal condition with MTM content of 20%,a flexible DSSC with overall light-to-electric energy conversion efficiency of 2.74%is achieved under a simulated solar light irradiation of 100 mW cm 2(AM 1.5),with 26%improvement in comparison with DSSCs based on P25 alone.展开更多
A counter electrode for dye-sensitized solar cell (DSSC) was prepared by coating poly(3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT:PSS) with high transparency and adhesion on a conducting FTO glass at lo...A counter electrode for dye-sensitized solar cell (DSSC) was prepared by coating poly(3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT:PSS) with high transparency and adhesion on a conducting FTO glass at low temperature. The surface morphology, conductivity, sheet resistance, redox properties and photoelectric properties of the PEDOT:PSS/carbon electrodes were observed using scanning electron microscopy, a four-probe tester and a CHI660D electrochemical measurement system. The experimental results showed that DSSCs had the best photoelectric properties for PEDOT:PSS/carbon counter electrodes annealed at 80°C under vacuum conditions. The overall energy conversion efficiency of the DSSC with PEDOT:PSS/carbon counter electrode and barrier layer reached 7.61% under irradiation from a simulated solar light with intensity of 100 mW/cm2 (AM 1.5). The excellent photoelectric properties, simple preparation procedure and low cost allow the PEDOT:PSS/carbon electrode to be a credible alternative electrode for use in DSSCs.展开更多
A microporous platinum/fullerenes (Pt/C 60) counter electrode was prepared by using a facile rapid thermal decomposition method,and the quantum-dot sensitized solar cell (QDSSC) of Pt/C 60-TiO 2-CdS-ZnS and Pt/C 60-Ti...A microporous platinum/fullerenes (Pt/C 60) counter electrode was prepared by using a facile rapid thermal decomposition method,and the quantum-dot sensitized solar cell (QDSSC) of Pt/C 60-TiO 2-CdS-ZnS and Pt/C 60-TiO 2-CdTe-ZnS was fabrication.The technique forms a good contact between QDs and TiO 2 films.The photovoltaic performances of the as-prepared cells were investigated.The QDSSCs with Pt/C 60 counter electrode show high power conversion efficiency of 1.90% and 2.06%,respectively (under irradiation of a simulated solar light with an intensity of 100 mW cm 2),which is comparable to the one fabricated using conventional Pt electrode.展开更多
基金supported by the National High Technology Research and Development Program of China (2009AA03Z217)the National Natural Science Foundation of China (90922028,50842027)
文摘An upconversion luminescence powder TiO2:(Er3+,Yb3+) is prepared by a hydrothermal method and used to fabricate dye-sensitized solar cell (DSSC).The TiO2:(Er3+,Yb3+) powder undergoes upconversion luminescence,converting infrared light which the dye can not absorb into visible light with wavelengths of 510-700 nm which the dye can absorb,increasing the photocurrent of the DSSC.TiO2:(Er3+,Yb3+) also acts as a p-type dopant,heightening the Fermi level of the oxide film,which increases the photovoltage of the DSSC.The best performance of the DSSC is found when the ratio of TiO2/luminescence powder is 1/3 in the luminescence layer.Under simulated solar irradiation of 100 mW cm-2 (AM 1.5),the DSSC containing TiO2:(Er3+,Yb3+) doping achieves a light-to-electricity energy conversion efficiency of 7.28% compared with 6.41% for the undoped DSSC.
基金supported financially by the National High Technology Research and Development Program of China(2009AA03Z217)the National Natural Science Foundation of China(90922028)+1 种基金the Key Project of Chinese Ministry of Education(211204)the Fund of Fujian Provincial Key Laboratory of Nanomaterials(NM10-5)
文摘Mesoporous TiO2microsphere(MTM)was synthesized via a simple solution route and then mixed with commercial TiO2(P25)to form highly homogeneous and stable TiO2colloid by simple hydrothermal treatment.The TiO2colloid was coated onto the plastic conductive substrate to prepare mesoporous TiO2film for flexible dye-sensitized solar cells(DSSCs)by low-temperature heat treatment.The influence of MTM content on the physicochemical properties of the flexible TiO2film was characterized by scanning electron microscope,transmission electron microscopy,X-ray diffraction,energy-dispersive X-ray spectrometer,N2adsorption-desorption isotherms,UV–vis absorption and diffuse reflectance spectra.It is revealed that with increasing the MTM content,the dye-loading capability of TiO2film and light-harvesting efficiency of flexible DSSCs are improved due to MTM having high surface area and acting as a light scattering center,respectively,resulting in the enhancement of photocurrent of flexible DSSCs.However,more and larger cracks having negative effect on the performances of flexible DSSCs are formed simultaneously.Under the optimal condition with MTM content of 20%,a flexible DSSC with overall light-to-electric energy conversion efficiency of 2.74%is achieved under a simulated solar light irradiation of 100 mW cm 2(AM 1.5),with 26%improvement in comparison with DSSCs based on P25 alone.
基金supported by the National High Technology Research and Development Program of China (2009AA03Z217)the National Natural Science Foundation of China (90922028)
文摘A counter electrode for dye-sensitized solar cell (DSSC) was prepared by coating poly(3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT:PSS) with high transparency and adhesion on a conducting FTO glass at low temperature. The surface morphology, conductivity, sheet resistance, redox properties and photoelectric properties of the PEDOT:PSS/carbon electrodes were observed using scanning electron microscopy, a four-probe tester and a CHI660D electrochemical measurement system. The experimental results showed that DSSCs had the best photoelectric properties for PEDOT:PSS/carbon counter electrodes annealed at 80°C under vacuum conditions. The overall energy conversion efficiency of the DSSC with PEDOT:PSS/carbon counter electrode and barrier layer reached 7.61% under irradiation from a simulated solar light with intensity of 100 mW/cm2 (AM 1.5). The excellent photoelectric properties, simple preparation procedure and low cost allow the PEDOT:PSS/carbon electrode to be a credible alternative electrode for use in DSSCs.
基金supported by the National High Technology Research and Development Program of China (2009AA03Z217)the National Natural Science Foundation of China (90922028 and 51002053)
文摘A microporous platinum/fullerenes (Pt/C 60) counter electrode was prepared by using a facile rapid thermal decomposition method,and the quantum-dot sensitized solar cell (QDSSC) of Pt/C 60-TiO 2-CdS-ZnS and Pt/C 60-TiO 2-CdTe-ZnS was fabrication.The technique forms a good contact between QDs and TiO 2 films.The photovoltaic performances of the as-prepared cells were investigated.The QDSSCs with Pt/C 60 counter electrode show high power conversion efficiency of 1.90% and 2.06%,respectively (under irradiation of a simulated solar light with an intensity of 100 mW cm 2),which is comparable to the one fabricated using conventional Pt electrode.