Effect of Nb on the corrosion behavior of continuous bulk metallic glass-coated steel wire composites

（Zr41.2Ti13.sCu12.sNi10Be22.5）100-~Nb~ （at%, x=0 and 8） bulk metallic glasses （BMGs） were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of these BMGs were conducted in 3.5wt% NaC1 aqueous solution. It is found that the addition of 8at% Nb into Zr41.2Ti13.sCu12.sNi10Be22.5 alloy results in the improvement of corrosion resistance with the pitting potential of -52 mV, the open circuit potential of-446 mV, and the corrosion current density of 9.86x 10-6 mA/cm2. This may be attributed to that Nb is beneficial to passivate and stabilize Zr and Ti.

Influence of Cu content on the mechanical properties and corrosion resistance of Mg-Zn-Ca bulk metallic glasses

（Mg66.aZn28.8Cas）10o-xCux （at%, x = 0, 1, 3, and 5） bulk metallic glasses （BMGs） of 2 mm in diameter were prepared by the conventional copper mold injection casting method. Besides, the influence of Cu content on the microstructure, thermal stability, mechanical properties, and corrosion behavior of Mg-Zn--Ca BMGs was investigated. It is found that the addition of Cu decreases the glass-forming ability of Mg-Zn-Ca BMGs. Crystalline phases are precipitated at a higher Cu content, larger than 3at%. The compressive fracture strength of Mg-Zn-Ca BMGs is enhanced by the addition of Cu. With the formation of in-situ composites, the compressive strength of the Mg-Zn-Ca alloy with 3at% Cu reaches 979 MPa, which is the highest strength among the Mg-Zn-Ca alloys. Furthermore, the addition of Cu also results in the increase of corrosion potential and the decrease of corrosion current density in Mg-Zn-Ca BMGs, thereby delaying their biodegradability.

Coating thickness control in continuously fabricating metallic glass-coated composite wires

A continuous production process was developed for coating bulk metallic glasses on the metallic wire surface. The effects of processing parameters, including the drawing velocity and coating temperature, on the coating thickness were investigated. It is found that the coating thickness increases with the increase in drawing velocity but decreases with the increase in coating temperature. A fluid mechanical model was developed to quantify the coating thickness under various processing conditions. By using this theoretical model, the coating thickness was calculated, and the calculated values are in good agreement with the experimental data.

High plastic Zr–Cu–Fe–Al–Nb bulk metallic glasses for biomedical applications

Four Zr–Cu–Fe–Al-based bulk metallic glasses（BMGs） with Zr contents greater than 65at% and minor additions of Nb were designed and prepared. The glass forming abilities, thermal stabilities, mechanical properties, and corrosion resistance properties of the prepared BMGs were investigated. These BMGs exhibit moderate glass forming abilities along with superior fracture and yield strengths compared to previously reported Zr–Cu–Fe–Al BMGs. Specifically, the addition of Nb into this quaternary system remarkably increases the plastic strain to 27.5%, which is related to the high Poisson＇s ratio and low Young＇s and shear moduli. The Nb-bearing BMGs also exhibit a lower corrosion current density by about one order of magnitude and a wider passive region than 316 L steel in phosphate buffer solution（PBS, pH 7.4）. The combination of the optimized composition with high deformation ability, low Young＇s modulus, and excellent corrosion resistance properties indicates that this kind of BMG is promising for biomedical applications.

Manufacturing process and microstructure of copper-coated aluminum wires

Copper-coated aluminum wires exhibit good electrical conductivity, high thermal conductivity, low contact resistance of copper and low density, and provide economic advantages over aluminum. However, there are some problems in the manufacring processes of hot-dip copper-coated aluminum wires, such as the difficulties in controlling coating process. In this work, the hot-dip copper-coating method of aluminum wires was investigated for producing copper-coated aluminum wire composites. The interface microstructure between the aluminum wire and the copper coating layer was analyzed by scanning electron microscopy （SEM） and energy-dispersive X-ray spec- trometry （EDS）. Five different fluxing agents were tested. Experimental results show that appropriate conditions for the hot-dip process are determined as the liquid copper temperature of 1085℃ and the treatment time less than 1 s. A success in hot-dip copper-coated aluminum wires is achieved by hot-dipping a low-melting-point metal into a high-melting-point metal liquid, which is significant for the further devel- opment and application of copper-coated aluminum wire composites.