Mechanical and magnetic properties as well as their relationship in the reduced activation martensitic （RAM） steel were investigated in the temperature range from -90℃ to 20℃. Charpy impact tests show that the duc...Mechanical and magnetic properties as well as their relationship in the reduced activation martensitic （RAM） steel were investigated in the temperature range from -90℃ to 20℃. Charpy impact tests show that the ductile-to-brittle transition temperature （DBTT） of the RAM steel is about -60℃. Low-temperature tensile tests show that the yield strength, ultimate tensile strength and total elongation values increase as temperature decreases, indicating that the strength and plasticity below the DBTT are higher than those above the DBTT. The coercive field （Hc） in the scale of logarithm decreases linearly with the increasing temperature and the absolute value of the slope of InHc versus temperature above the DBTT is obviously larger than that below the DBTT, also confirmed in the T91 steel. The results indicate that the non-destructive magnetic measurement is a promising candidate method for the DBTT detection of ferromagnetic steels.展开更多
文摘Mechanical and magnetic properties as well as their relationship in the reduced activation martensitic （RAM） steel were investigated in the temperature range from -90℃ to 20℃. Charpy impact tests show that the ductile-to-brittle transition temperature （DBTT） of the RAM steel is about -60℃. Low-temperature tensile tests show that the yield strength, ultimate tensile strength and total elongation values increase as temperature decreases, indicating that the strength and plasticity below the DBTT are higher than those above the DBTT. The coercive field （Hc） in the scale of logarithm decreases linearly with the increasing temperature and the absolute value of the slope of InHc versus temperature above the DBTT is obviously larger than that below the DBTT, also confirmed in the T91 steel. The results indicate that the non-destructive magnetic measurement is a promising candidate method for the DBTT detection of ferromagnetic steels.