The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron pr...The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron probe microanalysis(EPMA),and energy dispersive spectroscopy(EDS).The solidus and liquidus of single crystal alloy were obtained by differential scanning calorimetry(DSC).Results show that the mosaic-like eutectic and fan-like eutectic are dissolved at first,and the coarseγ'phase is dissolved later during the solution heat treatment of 1,390°C/2 h+1,310°C/4 h+1,320°C/10 h+air cooling(AC).The composition segregations of Al,Ta,W and Re are 0.99,0.96,1.04 and 1.16,respectively,which close to 1.The incipient melting is caused by the low local temperature of the alloy,and the micropore region with a lower melting point is the preferred position for incipient melting.展开更多
The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior exam...The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ' phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800℃; meanwhile, when the temperature is between 800℃ and 1000℃, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600℃ and 1000℃.展开更多
基金The authors would like to express their sincere thanks to the financial support from the Key Project of National Natural Science Foundation of China(No.U16642548).
文摘The evolution of microstructure and formation mechanism of incipient melting microstructure of DD5 single crystal superalloy during solution heat treatment were studied by scanning electron microscopy(SEM),electron probe microanalysis(EPMA),and energy dispersive spectroscopy(EDS).The solidus and liquidus of single crystal alloy were obtained by differential scanning calorimetry(DSC).Results show that the mosaic-like eutectic and fan-like eutectic are dissolved at first,and the coarseγ'phase is dissolved later during the solution heat treatment of 1,390°C/2 h+1,310°C/4 h+1,320°C/10 h+air cooling(AC).The composition segregations of Al,Ta,W and Re are 0.99,0.96,1.04 and 1.16,respectively,which close to 1.The incipient melting is caused by the low local temperature of the alloy,and the micropore region with a lower melting point is the preferred position for incipient melting.
基金financially supported by Jiangsu Industrial Support Project (Nos. BE2014007-2, BE2014007-3, and BE2014007-4)the financial support from Jiangsu Development and Reform Commission (No. [2013]2027)Jiangsu Postgraduates Innovating Scientific Research Project (No. KYLX15-1061)
文摘The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ' phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800℃; meanwhile, when the temperature is between 800℃ and 1000℃, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600℃ and 1000℃.