Preparation of ceramsite from solid waste based on the sintering process is a new technology and had a high efficiency in improving producing capability, decreasing consumption of liquefied petroleum gas (LPG), and re...Preparation of ceramsite from solid waste based on the sintering process is a new technology and had a high efficiency in improving producing capability, decreasing consumption of liquefied petroleum gas (LPG), and recovering waste heat of flue gas. An experiment sintering gangue ceramsite was conducted in a 25 kg scale sintering pot with a 100 cm height. The combustion characteristics, phase transformation, and the release profile of SO_(2)^(*) (SO and/or SO_(2)) and NO_(x)^(*) (N_(2)O, NO, and/or NO_(2)) of gangue ceramsite during the sintering process were studied by X-ray diffraction analysis, X-ray fluorescence spectrometry, thermogravimetry–differential thermogravimetry–differential scanning calorimetry, and measurement of physical properties of ceramsite and gas components of flue gas. The results showed that the gangue ceramsite had excellent properties, and its compressive strength and water absorption were 8.2–9.6 MPa and 8.9%–9.8%, respectively, far exceeding the requirement of standard (GB/T 17431.1–2010). The ignition temperature of gangue ceramsite was 443 ℃, and the ignition loss was 14.60 mass% at 1000 ℃. Kaolinite and calcite disappeared at 600 and 800 ℃, respectively. Albite disappeared and mullite formed at 1000 ℃. Two peaks of SO_(2)^(*) emissions emerged in the range of 311–346 mg m^(-3) near 500 ℃ of upper layer ceramsite and 420–489 mg m^(-3) near 1000 ℃ of lower layer ceramsite, respectively. NO_(x)^(*) emissions peak emerged in the range of 227–258 mg m^(-3) near 550 ℃ of the upper layer ceramsite, which was related to the oxidation of sulfide and the combustion of LPG. Gangue is a direct heat source for sintering of ceramsite as well. During sintering process, the heat of flue gas above and below 400 ℃ accounts for 55.9% and 30.0% of the all-output heat, respectively, and was potentially used for producing waste-heat steam or electricity as by-products and drying raw materials during its own initial sintering process, which can realize combined mass and heat utilization for the gangue and further reduce the cost of sintered gangue ceramsite.展开更多
基金support of the Shendong Buertai Colliery and Shandong ECON Energy Saving Technology Co.,Ltd on experimentssupport from the National Key R&D Program Project(Grant No.2019YFC1905705)is greatly acknowledged.
文摘Preparation of ceramsite from solid waste based on the sintering process is a new technology and had a high efficiency in improving producing capability, decreasing consumption of liquefied petroleum gas (LPG), and recovering waste heat of flue gas. An experiment sintering gangue ceramsite was conducted in a 25 kg scale sintering pot with a 100 cm height. The combustion characteristics, phase transformation, and the release profile of SO_(2)^(*) (SO and/or SO_(2)) and NO_(x)^(*) (N_(2)O, NO, and/or NO_(2)) of gangue ceramsite during the sintering process were studied by X-ray diffraction analysis, X-ray fluorescence spectrometry, thermogravimetry–differential thermogravimetry–differential scanning calorimetry, and measurement of physical properties of ceramsite and gas components of flue gas. The results showed that the gangue ceramsite had excellent properties, and its compressive strength and water absorption were 8.2–9.6 MPa and 8.9%–9.8%, respectively, far exceeding the requirement of standard (GB/T 17431.1–2010). The ignition temperature of gangue ceramsite was 443 ℃, and the ignition loss was 14.60 mass% at 1000 ℃. Kaolinite and calcite disappeared at 600 and 800 ℃, respectively. Albite disappeared and mullite formed at 1000 ℃. Two peaks of SO_(2)^(*) emissions emerged in the range of 311–346 mg m^(-3) near 500 ℃ of upper layer ceramsite and 420–489 mg m^(-3) near 1000 ℃ of lower layer ceramsite, respectively. NO_(x)^(*) emissions peak emerged in the range of 227–258 mg m^(-3) near 550 ℃ of the upper layer ceramsite, which was related to the oxidation of sulfide and the combustion of LPG. Gangue is a direct heat source for sintering of ceramsite as well. During sintering process, the heat of flue gas above and below 400 ℃ accounts for 55.9% and 30.0% of the all-output heat, respectively, and was potentially used for producing waste-heat steam or electricity as by-products and drying raw materials during its own initial sintering process, which can realize combined mass and heat utilization for the gangue and further reduce the cost of sintered gangue ceramsite.
